Exploration of Phyllanthus acidus mediated silver nanoparticles and its activity against infectious bacterial pathogen

Abstract

In our present investigation, synthesis of nontoxic, eco friendly and cost effective silver nanoparticles, Phyllanthus acidus (P. acidus) was used as starting material. The influence of phyto-constituents present in aqueous extracts of Phyllanthus acidus was found to be effective in reduction of silver nitrate to free silver nanoparticles (PA-AgNPs). HPTLC finger print analysis reveals the presence of flavonoid, quercetin in aqueous extracts of Phyllanthus acidus. Surface plasmon racemonance exhibited λ max at 462 nm through UV–Vis spectroscopy. Zeta size revealed that the size of nanoparticles were with in the range of 65–250 nm with polydisperse index (PDI) of 0.451. The negative charge of zeta potential value (− 16.4) indicates repulsion among PA-AgNPs with their excellent stability. FESEM-EDAX, XRD and TEM analysis confirmed the presence of nano-crystalline PA-AgNPs with different morphological textures. Further, PA-AgNPs has shown potent antibacterial effect on E. coli cells. The greater antibacterial effect (viable and dead cells) of PA-AgNPs were confirmed by using acridine orange (AO) dye which can able to provide insight of healthy as well as damaged DNA. Live cells emit florescence green and dead cells (treated with PA-AgNPS at 20 and 40 µg/ml) appear as pale orange red colour. Post treatment, investigations of PA-AgNPs on E. coli cells under SEM was found to be effective against cell membrane damages which leads to cell death or cell growth arrest. Hence, from the above findings, we strongly recommend silver nanoparticles from Phyllanthus acidus can be used as a potential source for antimicrobial agent for chronic infections and also against other harmful microorganisms.

Introduction

For years together, microbes are complicated and it was difficult to restrict their growth or to prevent its infection towards human beings. The current accessible drug regimen on prolonged treatment was making these microbial pathogens to become resistant and causing urge in need of newer anti microbial agents with superior mode of action [1, 2]. In recent days, nanotechnology and nano scale materials have emerged as potent delivery materials for many ailments [3]. This may be due to its size, unique surface area to volume ratio and chemical complexities has created a new platform to fight against many diseases. Among promising nano materials, metallic silver nanoparticles plays a pivotal role in exhibiting antibacterial property [4]. Many studies support that nanonization of silver found to be effective against various microbial pathogens like Staphylococcus aureus, Escherichia coli, Vibrio cholerae, Pseudomonas aeruginosa and Salmonella typhi [5, 6]. The recent available methods of fabrication of metallic silver nanoparticles are capital intensive, toxic, non eco-friendly and have low productivity leading towards the hunt for alternative and high capacitive nanoparticles. The biosynthesized routes otherwise called as “Green synthesis” methods were under wide exploration due to their amenability towards better biological functionalizations. The formation of silver nanoparticles were based on the type of solvent and nature of reducing agents (biomolecules) which acts as capping agent in the formation of free silver ions [6]. Such silver nanoparticles have wide range of application in various disciplines like (a) biological tags and biosensors in diagnostic applications, (b) incorporating Ag-NPs in apparel, footwear, wound dressings, paints, cosmetics and plastics resulted in antibacterial properties, (c) Ag-NPs as conductive inks in composites as enhanced thermal and electrical conductivity and (d) Ag-NPs exhibit as metal-enhanced fluorescence (MEF) and surface-enhanced Raman scattering (SERS) thus leading to optical applications.‘

Hence, our investigation was focused on fabrication of eco friendly silver nanoparticles by using green source, such as aqueous leaf extracts of Phyllanthus acidus (P. acidus) which had significant economic importance. However, Phyllanthus acidus was said to be having wide range of phytoconstituents including terpenoids, alkaloids, flavonoids and tannins, which have been shown to posse’s useful biological activity in in vitro and in vivo. Moreover, P. acidus claims as anti inflammatory, anticancer, antiplatelet, antipyretic, antiviral, antimutagenic, antiallergic and antibacterial. Here, we have reported a novel method for synthesis of silver nanoparticles from the leaves of P. acidus and its antimicrobial potential against E. coli cells.

Materials and methods

Materials

All chemicals used in this study were obtained from Sigma (Bangalore, India) and Merck (Mumbai, India). Phyllanthus acidus leaves were collected from the local area of Srivilliputtur and authenticated by Dr. Madav Shetty, Professor, Department of Botany, S.V. University, Tirupati. Voucher specimen (AKCP-PH-0254) was deposited in the Pharmacognosy Laboratory, Arulmigu Kalasalingam College of Pharmacy, Krishnankoil, India.

Preparation of P. acidus extract

Fresh leaves of P. acidus (200 g) were collected in the month of February. The leaves were brought to DDN lab and washed with double distilled water to get rid of dust particulates present on them. The leaves were reduced to tiny size and shade dried for 1 week. The material was powdered (Coarse) by using mixer grinder and then sieved to get fine particles. About 100 g of powder was suspended in 400 ml of double distilled water, heated at 65 °C for 60 min, filtered through Watman filter paper No. 2 and the filtrate was stored in the refrigerator at − 4 °C for further experimental purpose.

Preliminary phytochemical screening and HPTLC finger print analysis

Preliminary phytochemical analysis for P. acidus extracts were carried out as per the protocol mentioned in Harbore, 1998 [7]. HPTLC (silica gel G 60F254 TLC plates of E. Merck, layer thickness 0.2 mm) fingerprint analysis was established for aqueous extracts of P. acidus. HPTLC was performed on (10 cm × 10 cm) aluminum backed plates coated with silica gel 60F254 (Merck, Mumbai, India). Standard solution of quercetin and test were applied on the plates as bands of 8.0 mm wide, 30.0 mm apart, and 10.0 mm from the bottom edge of the same chromatographic plate by use of Camag (Muttenz, Switzerland) Linomat V sample applicator equipped with 100 µl Hamilton (USA) syringe. Ascending development to a distance of 80 mm was performed at room temperature (28 ± 2 °C), with toluene:ethyl acetate:formic acid [(5:4:1) (v/v/v)], as mobile phase in a Camag glass twin trough chamber previously saturated with mobile phase vapour for 20 min, Quercetin of (100 µg/ml) was used as standard [8].

Synthesis of Phyllanthus acidus (PA-AgNPs) silver nanoparticles

Aqueous solution (1 mM) of silver nitrate (AgNO3; mol. wt: 169.87) was prepared and used for the synthesis of P. acidus silver nanoparticles (PA-AgNPs). Pipette out 400 µl of extracts (previously extracted and stored), added to 40 ml of 1 mM AgNO3 solution and kept in shaker for 10 min to promote the reduction. The reaction mixture was set to continue for 24 h in the dark at a temperature of (25 ± 2 °C). The silver nanoparticles thus obtained were purified by repeated centrifugation at 10,000 rpm for 10 min followed by redispersion in milliQ water [9].

Characterization studies

The absorption spectra for synthesized silver nanoparticles (PA-AgNPs) were measured by using a Shimadzu spectrophotometer (UV-1700) at 300–800 nm range. Particle size and zeta potential were assessed by using HORIBA Instruments (Singapore) Pvt Ltd, Singapore [10]. For X-ray diffraction (XRD) analysis, PA-AgNPs sample was spread on thin aluminium foil by dropping 100 µl of sample, dried at 50 °C and subjected into Rigaku smart lab instrument, operated at a voltage of 40 kV 30 mA current having Cu Kα1 radiations [11]. Size and elemental composition was confirmed by using Field emission scanning electron microscopy-energy dispersive X-ray analysis (FESEM-EDAX) by SUPRA 55-CARL ZEISS, Germany. The morphology and size were further confirmed by Transverse electron microscopy (TEM) by coating onto carbon coated grids performed by JEOL 3010 instrument, operated at an accelerating voltage of 300 kV.

Antibacterial activity of PA-AgNPs against E. coli by agar well diffusion techinique

For antibacterial evaluation of PA-AgNPs, Escherichia coli (MTCC 443) was selected as target organism. Prior to experimentation, E. coli cells were subcultured by using nutrient broth and Muller Hinton Agar (MHA) plates were prepared for antibacterial assay. Bacterial suspension was swabbed on MHA plates. Three wells (6 mm diameter) were pierced and test samples (10 and 20 µg/ml of PA-AgNPs) and standard (15 µg/ml of streptomycin sulfate) were seeded in to the wells and zone of inhibition was measured after 18 h of  incubation [12].

Effect of PA-AgNPs on E. coli cell surface morphology

The change in surface morphology of E. coli was examined after treating with PA-AgNPs at 20 µg/ml [13]. Post treatment, samples were kept in a shaker incubator at 150 rpm for 6 h. After treatment, a small drop of culture was fixed on glass grids (8 mm × 8 mm) with micro pipette, treated with graded methanol (to eliminate moisture in bacterial cell) with a method of critical-point drying [14]. The same procedure was repeated for untreated cells. Morphological changes in E. coli was examined using scanning electron microscope (SEM) JEOL-JSM-6060 model at 15–20 kV range.

Live and dead cells assay

Live and dead cell assessment was carried out for PA-AgNPs by using acridine orange (HiMedia laboratories, India) as staining reagent [15]. The stock was prepared by mixing of 0.05 ml of 1% Acridine orange with 5 ml of acetate buffer with 0.2 M (pH 4.0). Bacterial sample (E. coli) was spread on sterile glass slide, dried at 50 °C, fixed in absolute methanol for 2 min and air dried. The slides were then covered with acridine orange (AO) for 1 min, gently rinsed with tap water and air dried [16]. The samples were examined with epifluorescence microscope at 460–490 nm excitation (Eclipse 80i, Nikon, Japan).

Results and discussion

Preliminary phytochemical screening and HPTLC finger print analysis

Preliminary phytochemical investigation divulges the presence of glycosides, phenolic compounds, flavonoids, proteins, amino acids, carbohydrates and saponins in aqueous extracts of P. acidus. Hence, P. acidus extract containing higher altitude of phytoconstituents which may possibly take part in reactions in effective reduction of silver to free silver ions [17]. However, HPTLC finger print analysis also confirms the presence of quercetin (Fig. 1) flavonoid which has influenced the conversion of Ag+ to Ag0 ions due to easily oxidizable conjugated hydroxyl groups in the molecule [18].

Fig. 1
figure 1

HPTLC finger print analysis of P. acidus extracts

Synthesis of Phyllanthus acidus (PA-AgNPs) silver nanoparticles

Synthesis of silver nanoparticles were carried out in the presence of aqueous leaf extracts of Phyllanthus acidus. The color change was very rapid after addition of P. acidus extracts which turns the solution into brown within 10 min and turned to dark brown after 2 h. Color change from pale yellow to dark brown (Fig. 2) remained constant even after 24 h, which indicates the preliminary confirmation of formation of silver nanoparticles. It may be due to the reduction of silver nitrate into free silver nanoparticles by the influence of various conjugated hydroxyl groups present in the P. acidus extracts [19].

Fig. 2
figure 2

Preliminary conformation of formation of PA-AgNPs

Characterization studies

UV–Vis spectra of synthesized PA-AgNPs (Fig. 3) reveals the sharp intensity peak at 462 nm which was assumed to correspond to the silver nanoparticles. This excitation is due to induced electromagnetic field among nanoparticles by collective oscillation and conduction of electrons [20]. Particle size (Fig. 4) determination of synthesized PA-AgNPs were shown under by intensity. Laser diffraction reveals that particles obtained are in polydisperse (PI − 0.458) with the size range of 65–250 nm. Zeta potential of the synthesized (Fig. 5) PA-AgNPs was found to be − 23.8. The negative amplification by surface charge among nanoparticles could increase the electrostatic repulsion and repress the agglomeration which retains the particles as highly stable [21]. XRD is a commonly used method to determine the crystal structures of nanoparticles. X-ray diffraction (XRD) pattern of PA-AgNPs (Fig. 6) were compared with standard XRD files of PA-AgNPs published by the Joint Committee on Powder Diffraction Standards (JCPDS file no. 89-3722). Intense peaks occurred at 2θ peak values at 38.11°, 44.23°, 64.43° and 77.49° corresponds to (111), (200), (220) and (311) set of lattice planes respectively [22]. The pattern of silver nano particles were further confirmed by FESEM-EDAX (Fig. 7). The size (diameter) was clearly distinguishable at 200 nm range. The outcome of FESEM information (Fig. 8) was overlayed with earlier reports [23, 24]. The strong signal peak of silver in the synthesized product was due to surface plasmon racemonance, confirmed by EDAX analysis at 3 keV. Moreover, weaker signals from oxygen and other atoms were observed and this may be due to the bounce of biomolecules on to the surface of synthesized PA-AgNPs [25]. TEM studies reveals exact shape and size of the PA-AgNPs. Figure 9 shows spherical and polydispersed silver nanoparticles formed by using aqueous extracts of Phyllanthus acidus leaves. It is quite interesting that these nanoparticles were encapsulated/bounded with organic biomolecules from the leaf extract [26].

Fig. 3
figure 3

UV–Vis spectrum of PA–AgNPs mediated through Phyllanthus acidus

Fig. 4
figure 4

Particle size distribution of PA-AgNPs

Fig. 5
figure 5

Zeta potential of synthesized PA-AgNPs

Fig. 6
figure 6

X-ray diffraction (XRD) pattern showing peaks for PA-AgNPs

Fig. 7
figure 7

EDAX profiles of synthesized PA-AgNPs

Fig. 8
figure 8

Scanning electron microscopy shows the various size ranges of formed silver nanoparticles (PA-AgNPs)

Fig. 9
figure 9

TEM micrograph image of bio-reduced silver nanoparticles (PA-AgNPs)

Antibacterial activity of PA-AgNPs against E. coli by agar well diffusion techinique

Antibacterial assay was carried out in triplicates by agar well diffusion technique, which is a regular technique used to estimate the sensitivity of microbial strains against a wide range of antibiotics at different concentrations in order to prove as potent antimicrobial agent. Figure 10 reveals that the antibacterial effect of PA-AgNPs against gram negative bacteria in terms of zone of inhibition at 10 µg/ml (24 mm) and 20 µg/ml (36 mm) which were compared to that of standard streptomycin sulphate at concentration of 15 µg/ml (39 mm). The possible mechanism behind formation of clear zones were due to the interference of silver nanoparticles on the bacterial cell proliferation [27].

Fig. 10
figure 10

Antibacterial activity of PA-AgNPs against gram negative bacteria (E. coli). Test (T1—10 µg/ml; T2—20 µg/ml; STD—15 µg/ml)

Effect of PA-AgNPs on E. coli cell surface morphology

The cell surface morphology of E. coli was extensively studied by using scanning electron microscopy. Post treatment with PA-AgNPs at the concentration of 20 µg/ml has shown the significant effect on the E. coli cell membrane which was compared with control. Figure 11b exhibits the formation of rumples, large surface collapses, abnormal cell breaking and complete lysis or dead cell formation in PA-AgNPs treated cells, whereas such kind of impressions were completely absent in untreated E. coli cells (Fig. 11a). Surface collapse and other abnormalities in E. coli was due to direct interference of PA-AgNPs on cellular biochemical process by pertaining interactions with thiol and amino groups in proteins associated with nucleic acids within cell membranes [28, 29]. This disruption of the cell wall is by direct production of increased levels of reactive oxygen species (ROS), mostly hydroxyl radicals and singlet oxygen causing interruption of cellular functions and leads to disorganization of membrane [30, 31]. However, the above said fact may be high in case of E. coli due to surface collapse of the cell wall which is less dense and it easily facilitates the inward flow of PA-AgNPs. Futher, these PA-AgNPs cause distinct damage to respiratory chain dehydrogenases, thus leading to cell cycle arrest or cell death [6, 32].

Fig. 11
figure 11

Morphological changes of E. coli cells under scanning electron microscopy before (a) and after (b) treatment with PA-AgNPS at 20 µg/ml

Live and dead cell assay

Bacterial assay (live and dead cell) was performed by using gram negative E. coli strains after 6 h post treatment with synthesized silver nanoparticles using Acridine orange (AO) as staining dye. The bacteria without addition of PA-AgNPs served as the control [33]. Under florescence microscope, viable cells appear as green whereas, nonviable cells appears as pale orange red color [34]. This green emittance under fluorescence microscope was due to passage of acridine orange (AO) dye through cell membrane and uptake of AO by internal cellular organelles. Figure 12a elicits florescence green colour at 460–490 nm due to electrostatic interaction of cationic dye deposition of AO on cell organelles [35]. Whereas, Fig. 12b emits pale orange red color by the direct influence of PA-AgNPs on intercalating regions of DNA, which breaks of ds DNA into ss RNA or ss DNA by that cells were dead and lost its potency in uptake of AO [36]. Hence, it reflects with pale orange red colors under florescence microscopy due to the presence of unwinded ds DNA [37].

Fig. 12
figure 12

Fluorescence images of E. coli cells, a live cells and b dead cells

Conclusion

The present investigation enlightens the fabrication of simple, clean, efficient, cost effective and eco friendly stable silver nanoparticles from aqueous leaf extracts of Phyllanthus acidus. Whereas, P. acidus extracts were effectively broke down the Ag+ ions into Ag0 in short time. The synthesized nanoparticles were characterized by using UV–Vis spectrum, Zeta size and potential, XRD, FESEM-EDAX and TEM. Further, the PA-AgNPs were said to be having promising effect on gram −ve bacteria, such as E. coli by proving excellent antibacterial activity on cell growth inhibition. Hence, this research concludes that Phyllanthus acidus mediated nanoparticles can be used against wide range of bacterial pathogens and it could be the pavement for newer formulations in near future for large scale applicator in the field of drug discovery.

References

  1. Lavakumar V, Masilamani K, Ravichandiran V, Venkateshan N, Saigopal DVR, Ashok Kumar CK, Sowmya C (2015) Promising upshot of silver nanoparticles primed from Gracilaria crassa against bacterial pathogens. Chem Central J 9(42):1–8

    CAS  Google Scholar 

  2. Pethakamsetty L, Kothapenta K, Nammi HR, Ruddaraju LK, Kollu P, Yoon SG, Pammi SVN (2017) Green synthesis, characterization and antimicrobial activity of silver nanoparticles using methanolic root extracts of Diospyros sylvatica. J Environ Sci 55:157–163

    Article  Google Scholar 

  3. Morones JR, Elechiguerra JL, Camacho A, Holt K, Kouri JB, Ramirez JT, Yacaman MJ (2005) The bactericidal effect of silver nanoparticles. Nanotechnology 16(10):2346–2353

    Article  CAS  Google Scholar 

  4. Ping G, Huimin L, Xiaoxiao H, Kemin W, Jianbing H, Weihong T, Shouchun Z, Xiaohoi Y (2007) Preparation and antibacterial activity of Fe3O4@Ag nanoparticles. Nanotechnology 18(28):285604

    Article  Google Scholar 

  5. Moyer CA, Brentano L, Gravens DL, Margraf HW, Monafo WW Jr (1965) Treatment of large human burns with 0.5 per cent silver nitrate solution. Archiv Surg (Chicago, Ill: 1960) 90:812–867

    Article  CAS  Google Scholar 

  6. Li WR, Xie XB, Shi QS, Zeng HY, Ou-Yang YS, Chen YB (2010) Antibacterial activity and mechanism of silver nanoparticles on Escherichia coli. Appl Microbiol Biotechnol 85(4):1115–1122

    Article  CAS  Google Scholar 

  7. Paterson (1999) Phytochemical methods. A guide to modern techniques of plant analysis. Plant Pathol 48(1):146–148

    Article  Google Scholar 

  8. Vijayalakshmi A, Ravichandiran V, Malarkodi V, Nirmala S, Jayakumari S (2012) Screening of flavonoid “quercetin” from the rhizome of Smilax china Linn. for anti-psoriatic activity. Asian Pac J Top Biomed 2(4):269–275

    Article  CAS  Google Scholar 

  9. Padalia H, Moteriya P, Chanda S (2015) Green synthesis of silver nanoparticles from marigold flower and its synergistic antimicrobial potential. Arab J Chem 8(5):732–741

    Article  CAS  Google Scholar 

  10. Mallikarjuna K, Narasimha G, Dillip GR, Praveen B, Shreedhar B, Sree Lakshmi C, Reddy BV, Deva Prasad RB (2011) Green synthesis of silver nanoparticles using Ocimum leaf extract and their characterization. Digest J Nanomater Biostruct 6(1):181–186

    Google Scholar 

  11. Subba Rao Y, Kotakadi VS, Prasad TNVKV, Reddy AV, Sai Gopal DVR (2013) Green synthesis and spectral characterization of silver nanoparticles from Lakshmi tulasi (Ocimum sanctum) leaf extract. Spectrochim Acta Part A Mol Biomol Spectrosc 103:156–159

    Article  CAS  Google Scholar 

  12. Shahverdi AR, Fakhimi A, Shahverdi HR, Minaian S (2007) Synthesis and effect of silver nanoparticles on the antibacterial activity of different antibiotics against Staphylococcus aureus and Escherichia coli. Nanomedicine 3(2):168–171

    Article  CAS  Google Scholar 

  13. Choi Y, Kim HA, Kim KW, Lee BT (2017) Comparative toxicity of silver nanoparticles and silver ions to Escherichia coli. J Environ Sci 66:50–60

    Article  Google Scholar 

  14. Sener A, Erkin Y, Sener A, Tasdogen A, Dokumaci E, Elar Z (2015) In vitro comparison of epidural bacteria filters permeability and screening scanning electron microscopy. Rev Bras Anestesiol 65(6):491–496

    Article  Google Scholar 

  15. Hobbie JE, Daley RJ, Jasper S (1977) Use of nuclepore filters for counting bacteria by fluorescence microscopy. Appl Environ Microbiol 33(5):1225–1228

    CAS  Google Scholar 

  16. Kasten FH (1967) Cytochemical studies with acridine orange and the influence of dye contaminants in the staining of nucleic acids. Int Rev Cytol 21:141–202

    Article  CAS  Google Scholar 

  17. Martinez-Perez C, Ward C, Cook G, Mullen P, McPhail D, Harrison DJ et al (2014) Novel flavonoids as anti-cancer agents: mechanisms of action and promise for their potential application in breast cancer. Biochem Soc Trans 42(4):1017–1023

    Article  Google Scholar 

  18. Terenteva EA, Apyari VV, Dmitrienko SG, Zolotov YA (2015) Formation of plasmonic silver nanoparticles by flavonoid reduction: a comparative study and application for determination of these substances. Spectrochim Acta Part A Mol Biomol Spectrosc 151:89–95

    Article  CAS  Google Scholar 

  19. Mukherjee P, Roy M, Mandal BP, Dey GK, Mukherjee PK, Ghatak J et al (2008) Green synthesis of highly stabilized nanocrystalline silver particles by a non-pathogenic and agriculturally important fungus T. asperellum. Nanotechnology 19(7):075103

    Article  CAS  Google Scholar 

  20. McCarthy LR, Senne JE (1980) Evaluation of acridine orange stain for detection of microorganisms in blood cultures. J Clin Microbiol 11(3):281–285

    CAS  Google Scholar 

  21. Suttiponparnit K, Jiang J, Sahu M, Suvachittanont S, Charinpanitkul T, Biswas P (2011) Role of surface area, primary particle size, and crystal phase on titanium dioxide nanoparticle dispersion properties. Nanoscale Res Lett 6(1):27–30

    Google Scholar 

  22. Stalin Dhas T, Ganesh Kumar V, Stanley Abraham L, Karthick V, Govindaraju K (2012) Sargassum myriocystum mediated biosynthesis of gold nanoparticles. Spectrochim Acta Part A Mol Biomol Spectrosc 99:97–101

    Article  CAS  Google Scholar 

  23. Ahmad N, Sharma S, Rai R (2012) Rapid green synthesis of silver and gold nanoparticles using peels of Punica granatum. Adv Mater Lett 3(5):376–380

    Article  CAS  Google Scholar 

  24. Phanjom P, Zoremi E, Mazumder J, Saha M, Baruah SB (2012) Green synthesis of silver nanoparticles using leaf extract of Myrica esculenta. Int J Nanosci Nanotechnol 3:73–79

    Google Scholar 

  25. Magudapathy P, Gangopadhyay P, Panigrahi BK, Nair KGM, Dhara S (2001) Electrical transport studies of Ag nanoclusters embedded in glass matrix. Phys B Condens Matter 299(1–2):142–146

    Article  CAS  Google Scholar 

  26. Iravani S (2011) Green synthesis of metal nanoparticles using plants. Green Chem 13(10):2638–2650

    Article  CAS  Google Scholar 

  27. Kannan N, Subbalaxmi S (2011) Green synthesis of silver nanoparticles using Bacillus subtillus IA751 and its antimicrobial activity. Res J Nanosci Nanotechnol 1(2):87–94

    Article  Google Scholar 

  28. Choi O, Deng KK, Kim NJ, Ross L Jr, Surampalli RY, Hu Z (2008) The inhibitory effects of silver nanoparticles, silver ions, and silver chloride colloids on microbial growth. Water Res 42(12):3066–3074

    Article  CAS  Google Scholar 

  29. Brett DW (2006) A discussion of silver as an antimicrobial agent: alleviating the confusion. Ostomy Wound Manag 52(1):34–41

    Google Scholar 

  30. Brayner R, Ferrari-Iliou R, Brivois N, Djediat S, Benedetti MF, Fievet F (2006) Toxicological impact studies based on Escherichia coli bacteria in ultrafine ZnO nanoparticles colloidal medium. Nano Lett 6(4):866–870

    Article  CAS  Google Scholar 

  31. Tran N, Tran PA (2012) Nanomaterial-based treatments for medical device-associated infections. ChemPhysChem 13(10):2481–2494

    Article  CAS  Google Scholar 

  32. Zhang L, Jiang Y, Ding Y, Povey M, York D (2007) Investigation into the antibacterial behaviour of suspensions of ZnO nanoparticles (ZnO nanofluids). J Nanopart Res 9(3):479–489

    Article  Google Scholar 

  33. Korgaonkar KS, Ranade SS (1966) Evaluation of acridine orange fluorescence test in viability studies on Escherichia coli. Can J Microbiol 12(1):185–190

    Article  CAS  Google Scholar 

  34. Strugger S (1948) Fluorescence microscope examination of bacteria in soil. Can J Res 26(2):188–193

    Article  CAS  Google Scholar 

  35. Mayor HD, Hill NO (1961) Acridine orange staining of a single-stranded DNA bacteriophage. Virology 14:264–266

    Article  CAS  Google Scholar 

  36. Armstrong JA (1956) Histochemical differentiation of nucleic acids by means of induced fluorescence. Exp Cell Res 11(3):640–643

    Article  CAS  Google Scholar 

  37. Rodrigues UM, Kroll RG (1986) Use of the direct epifluorescent filter technique for the enumeration of yeasts. J Appl Bacteriol 61(2):139–144

    Article  CAS  Google Scholar 

Download references

Authors’ contributions

LKV and SC has designed, performed and wrote the manuscript. NV has contributed for XRD interpretations. VR and DVRS helped to carry out cell membrane damage experiments. All authors read and approved the final manuscript.

Acknowledgements

The authors are grateful to T.N.K.V. Prasad, Institute of Frontier Technology, Regional Agricultural Research Station, Acharya N.G. Ranga Agricultural University, Tirupati for helping us to carry out particle size analysis. The authors also thankful to Center for Nanotechnology, Sathyabhama University, Chennai for carrying out FESEM and XRD studies. The authors extends sincere thanks to Prof. O. Mahammad Hussain, Thin Film Laboratory, Department of Physics, Sri Venkateswara University, Tirupati for providing SEM facilities to carry out this work. The authors are also thankful to management of Arulmigu Kalasalingam College of Pharmacy for providing all necessary facilities to carry out this work.

Competing intrests

The authors declare that they have no competing intrests.

Ethics approval and consent to participate

Not applicable.

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Vuppalapati Lavakumar.

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Sowmya, C., Lavakumar, V., Venkateshan, N. et al. Exploration of Phyllanthus acidus mediated silver nanoparticles and its activity against infectious bacterial pathogen. Chemistry Central Journal 12, 42 (2018). https://doi.org/10.1186/s13065-018-0412-7

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s13065-018-0412-7

Keywords