- Research article
- Open Access
Methyl oleate deoxygenation for production of diesel fuel aliphatic hydrocarbons over Pd/SBA-15 catalysts
© Lee and Ramli; licensee Chemistry Central Ltd. 2013
- Received: 22 May 2013
- Accepted: 2 September 2013
- Published: 5 September 2013
Catalytic deoxygenation is a prominent process for production of renewable fuels from vegetable oil. In this work, deoxygenation of technical grade methyl oleate to diesel fuel aliphatic hydrocarbons (C15 – C18) is evaluated with several parameters including temperature, hydrogen pressure and reaction time in a stirred batch reactor over Pd/SBA-15 catalysts.
Two different SBA-15 morphologies i.e. spherelike and necklacelike structures have been synthesize as supports for Pd active metal. It is found that Pd dispersion on necklacelike SBA-15 is higher than that of spherelike SBA-15. Notably, higher Pd dispersion on necklacelike SBA-15 provides significant deoxygenation efficiency as compared to Pd/SBA-15-spherelike. Results show that H2 pressures greatly determine the total ester conversion and selectivity to C15 – C18 aliphatic hydrocarbons. Total ester conversions with 55< selectivity to n-heptadecane are achieved using Pd/SBA-15-necklacelike at 270°C and 60 bar H2 pressure within 6 h reaction time. Gas phase study reveals that formation of C17 is generated via indirect decarbonylation when the reaction time is prolonged.
Pd/SBA-15-necklacelike catalyst exhibits good catalytic performance with high selectivity to diesellike aliphatic hydrocarbons (C15 – C18). The physicochemical properties of the Pd supported on different SBA-15 morphologies influence the deoxygenation activity of the catalysts. Furthermore, the reaction pathways are governed by the H2 pressure as well as reaction duration.
- Methyl Oleate
- Aliphatic Hydrocarbon
- Paraffinic Hydrocarbon
- Ethyl Stearate
- NiMo Catalyst
Currently, transportation fuel i.e. gasoline, diesel fuel and kerosene are obtained from crude oil refining . Alternative fuels are being sought to overcome the problem associated with dwindling oil reserves and stringent environmental restrictions in greenhouse emissions. To date, government regulations strongly promote utilization of alternative fuels in the effort to reduce the green house gases (GHG) emission as underlined in Kyotol Protocol [2, 3]. One of the approaches is to investigate the feasibility of vegetable oils to be the potential source for renewable fuels. Several technologies have been discovered to convert the triglycerides into biofuel like derivative of fatty acid methyl ester (FAME) from transesterification of fatty acid [4, 5], hydrocracking of biofeedstock into fuel range hydrocarbons [6, 7], hydrotreating of triglycerides and fatty acids into hydrocarbon middle distillates as well as production of renewable diesel followed by deoxygenation [8–11]. Although biodiesel production via transesterification is on commercial scale however, this process is highly sensitive to feedstock purity and the higher oxygen content of FAME exhibits poor fuel properties . Thus, biodiesel produced is not compatible for the current combustion engine. Deoxgenation of biofeedstock via hydrodeoxygenation (HDO) or pyrolysis provides an alternative route to produce renewable fuels which can be used as a direct replacement for petroleum sourced hydrocarbons. Nowadays HDO process has been industrialized to form diesel fuel from vegetable oils. Removal of oxygen from triglycerides at elevated temperatures over heterogeneous catalyst in the presence of H2 produces long-chain alkanes from C4 to C24, typically C16 to C18[13–16].
Supported metal sulfides, NiMo and CuMo sulfides, are the industrialized catalysts for hydroprocessing of petroleum-based feeds. Similarly, these conventional hydrotreating catalysts have been utilized to up-grade vegetable oils to a hydrocarbon-based fuel . Application of this process with the established existing hydroprocessing usually used in a petroleum refinery could eliminate the additional capital costs in construction of new infrastructure. However, metal sulfides used are required with careful handling for the process as well as has to mind for the risk of product with sulfur contamination .
Recently, development of sulfur free catalysts was the new approach for transformation of renewable sources into paraffinic liquid fuel. Senol et. al. has reported that catalytic HDO with unsulfided NiMo catalyst is favoured in generating hydrocarbon s with odd number of carbon atoms while sulfided catalyst preferably yield hydrocarbons with even number atoms.
Murzin and co-workers have extensively investigated deoxygenation of triglycerides model compounds such as fatty acids and methyl esters over supported metal catalysts [11, 19–21]. Commercial palladium (Pd) supported on activated carbon displayed as the most efficient catalyst in the deoxygenation of stearic acid at a reaction temperature of 300°C and 17 bar of 5 vol< H2/Ar1. Several reports revealed that supported Pd and Pt catalysts have high selectivity to form hydrocarbons with one carbon less than the corresponding fatty acids in the deoxygenation reaction while formation of CO and CO2 as the main gaseous products proposed that decarboxylation and decarbonylation were the primary reaction routes [21–25].
Immer et al. provided insight for gas phase composition in catalytic deoxygenation of free fatty acids (FFA) using Pd/C catalysts. There was found that deoxygenation pathway is sensitive to the H2 partial pressure applied in the system. Madsen et al. evaluated HDO activities for model fat mixture over Pt/γ-Al2O3 under different reaction conditions using a batch reactor and C15 – C18 diesel-like hydrocarbons were formed under H2 rich atmosphere.
To reduce the impact of internal mass transfer limitations and pore blockage, batch deoxygenation of ethyl stearate was studied using Pd supported on the siliceous mesocellular foam (MCF) . However, the study showed that less than 15< conversion of ethyl stearate was observed at 300°C under N2 atmosphere.
Stucky and co-workers discovered hexagonal mesoporous molecular silica that is Santa Barbara amorphous No. 15 (SBA-15) in 1998 . High surface area, large pore volume, high thermal and hydrothermal stabilities and well-defined pore size are the unique characteristics of SBA-15 to use as potential material in catalysis, adsorption, nanoelectronics and etc[29–31]. SBA-15 could be tailored out into different morphologies such as spheres , fibers  and rodlike  through monitoring of the synthesis conditions, thus having different physicochemical properties. The synthetic conditions including acid source [34, 35], weight ratio P123/silica source , temperature [37, 38], water content , pH value , addition of organic salt  and shearing flow  are the determining factors in fabrication of different forms of SBA-15. Differences in mesophase morphology may be significant for targeted application such as catalysis, separation, internal surface modification and bioimmobilization.
Pd/SBA-15 nanocomposite prepared by Wang et al. demonstrated superior catalytic activity and recyclability for Heck carbon-carbon coupling reaction. Besides, Pd/SBA-15 was also reported showing superior catalytic activity in deoxygenation of stearic acid at 300°C under 17 bar of 5 vol< H2/Ar as compared to Pd/C, the conventional deoxygenation catalyst . Hydrodeoxygenation of methyl oleate was studied over Ni2P/SBA-15 in a fixed-bed reactor and showed that uniform dispersion of NiP on SBA-15 resulted in higher conversion of esters and selectivity of long-chain paraffin .
Supported Pd on SBA-15 with 3 wt< as well as 5 wt< were tested for deoxygenation of stearic acid. The catalyst with 3 wt< showed highest catalytic activity and provided 90< n-heptadecane selectivity . Nevertheless, it found that 3.8 wt< supported Pd on SBA-15 was the optimum Pd loading for deoxygenation of methyl oleate . In this regard, catalytic deoxygenation of methyl oleate to C15 – C18 aliphatic hydrocarbons which are the major components find in diesel fuel is investigated over supported 3.8 wt< Pd nanoparticles on two different SBA-15 mesostructures, necklacelike and spherelike, using batch stirred reactor. Methyl oleate is selected as a feedstock for this study is due to presence of major amount in fatty acid monoesters molecules which are mostly found in vegetable oil.
Phase structure and physicochemical characterization
The main characteristics of mesoporous silica SBA-15 and Pd/SBA-15 composites: S BET , specific surface area (m 2 /g), V p , pore volume (cm 3 /g), D p , average pore diameter (nm)
Actual Pd contentb(wt<)
3.8 wt< Pd/SBA-15-N
3.8 wt< Pd/SBA-15-S
BET surface area for both SBA-15 morphologies decreases significantly with Pd incorporation although minor changes in the specific pore volume are observed.
H2 pulse chemisorption is used to measure Pd dispersion adsorbed on SBA-15 surface (Table 1). 39< Pd dispersion is found on necklacelike SBA-15 however, spherelike SBA-15 only provides 19< Pd dispersion.
Liquid phase deoxygenation of triglyceride surrogate molecules, methyl oleate to C15 – C18 aliphatic hydrocarbons is investigated in a stirred batch reactor over 3.8 wt< Pd/SBA-15 on two different SBA-15 morphologies as discussed before. Catalytic deoxygenation of methyl oleate (70< technical grade) is studied using Pd/SBA-15-necklacelike (N1) and Pd/SBA-15-spherelike (S1) catalysts at 270°C, 60 bar H2 pressure, catalyst loading of 3 wt< and 6 h reaction duration.
Total ester conversion with supported Pd on two different morphologies of SBA-15
BET surface area (m2/g)
Total ester conversion (<)
Figure 13 shows the evolution of gas-phase products with reaction time on 3.8< Pd/SBA-15-necklacelike at 270°C and 60 bar H2 pressure. CO2, CO and CH4 are evolved concomitantly during the reaction progression. Unlike the increase in the concentration of CO with time, the CO2 evolution decreases monotonically with reaction time. CO2/CO ratio is increased within 3 h reaction while subsequently there is a sharp decrease in CO/CO2 ratio (Figure 13). Besides, the methane content is increased remarkable in the total of carbonaceous gas products from 6 to 8 h reaction (Figure 13).
Ordered hexagonal pore array structure of SBA-15 with Pd incorporated is preserved since no significant change between the diffraction patterns which indexed as (100), (110) and (200) for Pd/SBA-15 and SBA-15 materials (Figure 1). However, it is observed that the intensity of the diffraction peaks at 2θ between 1.6 – 2.0° decreases significantly in necklacelike structure as compared to spherelike structure (inserted Figure 1). A decrease in peak intensity is attributed of distribution of the Pd on the external surface of the SBA-15. This means that more Pd particles are distributed on the external surface of necklacelike structure as compared to spherelike structure, thus resulted in a more significant reduction in surface area of necklacelike structure compared to spherelike structure.
A shift of the diffraction peaks to lower angles is identified from Pd/SBA-15 samples, reflecting an increase in unit cell parameter of the SBA-15 framework. As reported by other researchers [44–46], this feature is because of the metals substitution into mesoporous molecular sieves. Therefore, substitution of Pd into SBA-15 framework might be the main reason to increase the unit cell parameters of the SBA-15 mesoporous structure.
Hysteresis loop as observed in Figure 2 is due to the N2 capillary condensation in cylindrical mesoporous channels. Besides, no significant change of isotherm pattern from Pd/SBA-15 samples suggests that SBA-15 template is preserved with anchoring of Pd ion via impregnation. Necklacelike SBA-15 synthesized provides larger surface area and higher pore volume than spherelike SBA-15. This may be attributed to the formation of larger micelles quantity as a result of stirring during synthesis of necklacelike SBA-15. The micelles are then removed during calcination resulting in an increase in the number of pores thus an increase in the total surface area and total pore volume .
The significant reduction in surface area without significant decrease in pore volume (Table 1) may indicate that most of the PdO particles are distributed on the external surface of the support as compared to in the pores, thus resulted in a more significant reduction in the surface area as compared to the reduction in pore volume. However, wider pore distribution for Pd/SBA-15 samples was observed after incorporation of Pd in SBA-15 (Figure 3). As a result, the slight increase in average pore size of Pd-incorporated catalyst is due to an increase in pore distribution.
Better Pd distribution on necklacelike SBA-15 as compared to spherelike SBA-15 (Table 1) due to the most of the smaller PdO particles, ranged in 2–5 nm, are being formed on the surface of the necklacelike structure [Figure 7 (a)]. This may be attributed the larger surface area available in the necklacelike support, thus enable a better Pd dispersion. In addition, larger particle size found on spherelike SBA-15 is resulted from the agglomeration of PdO nanoparticles during calcinations process.
Stirring flow applied in reaction mixture governs the formation of different SBA-15 morphologies [32, 39]. Exerted shearing stress from continuous stirring promotes intermicelle interactions while short cylindrical silicate-surfactant micelles are lengthened along the flow direction and joined into longer silicas structure [Figure 4 (a)]. In addition, higher intensity of diffraction peaks at 2θ between 1.6 – 2.0° is observed for necklacelike SBA-15 as compared to spherelike SBA-15 (inserted Figure 1). Notably, the crystallinity of necklacelike SBA-15 is increased as the synthesis temperature was raised to 80°C. Therefore, it found that elongation of the longer silicas rod units under higher temperature leads to the formation of necklacelike SBA-15 structure.
It is found that better Pd/SBA-15-necklacelike contributes higher deoxygenation efficiency for aliphatic hydrocarbon formation instead of Pd/SBA-15-spherelike (Figure 8). The increased of surface-to-volume ratio due to higher Pd dispersion on necklacelike SBA-15 may enhance the adsorption of active Pd metal to methyl oleate molecules.
Pd/SBA-15-necklacelike catalyst is considered active over the temperature range studied as the total esters conversion achieved is more than 80< after 3 h reaction (Figure 9). It is observed that majority of methyl octadecanoate and methyl hexadecanoate are formed via hydrogenation of the unsaturated methyl esters as the reaction intermediates. Besides, the off-line gas analysis shows that CO2 is the main carbonaceous gas product.
Low selectivity of C15 to C18 aliphatic hydrocarbons (Figure 10) is due to saturation of dissolved H2 in reaction medium under high H2 pressure (80 bar), which active metal Pd interaction with methyl oleate molecules is inhibited like described by Madsen et al.. Reaction moves toward decarbonylation route in a presence of higher H2 pressure results decrease of CO2/CO ratio (Figure 11). The switchover phenomenon observed enhances the finding reported by Boda et al.  and Immer et al. studies . It is expected that methanation is facile under high H2 pressure condition like other reports mentioned . But it might be possible that minor methane formation is come from the CO hydrogenation as suggested by Donnis et al..
55< selectivity to n-heptadecane in 6 h reaction time demonstrates that Pd supported on necklacelike SBA-15 exhibits high deoxygenation efficiency to methyl oleate (Figure 12). In comparison to the work reported by Snare et al., only about 25< selectivity to the main product n-heptadecane was obtained from technical grade of methyl oleate using microporous Pd/C. Therefore, it is true to some extent that Pd/SBA-15 catalyst outperforms than Pd/C either using complex mixture of unsaturated esters in the present study or pure stearic acid itself . However, insufficient contact time for interaction of active metal Pd and methyl esters molecules into paraffinic hydrocarbons gives low selectivity of n-heptadecane in 1 h reaction.
As indicated in Figure 12, Pd supported on SBA-15 does not promote deoxygenation of fatty acids or ester functionalities via HDO pathway. In contrast, supported Pd catalyst is active in decarboxylation and/or decarbonylation route for elimination of C = O molecules to form odd-carbon-number of hydrocarbons. Isomers and unsaturated hydrocarbons are absence since Pd has been known as the strong hydrogenation agent. It is notably that isomerization and dehydrogenation are hardly involved in H2 atmosphere .
Production of CO and CO2 during decarboxylation/decarbonylation is crucial to understand plausible reaction path for the production of linear hydrocarbons. n-alkanes formation are preferable via decarboxylation within 3 h initial reaction time (as shown in Figure 13). However, highly dissolved H2 in the alkane solvent in a longer reaction time under high H2 pressure may push either decarbonylation or reverse water gas shift equilibrium towards increased CO formation in a gas phase. As previously showed in Figure 12 selectivity of n-heptadecane is significantly increased when reaction time is prolonged. As a result, switchover product selectivity from CO2 to CO observed reveals that conversion of methyl oleate to n-heptadecane is predominant via indirect decarbonylation. Methyl stearate, hydrogenated methyl oleate, proceeds via partial reduction of the carboxylic group to corresponding n-octadecanal followed by released of CO to form n-heptadecane as increasing of time-on-stream (Figure 14). High methanation of CO2 or CO attributes significant amount of methane in a gas phase as increased of reaction time. This finding shows that Pd/SBA-15 is active to reduce fully the oxidized carbon into methane.
Necklacelike SBA-15 with high surface area is a great support to disperse Pd nanoparticles. Nanosized Pd particles anchored on necklacelike SBA-15 shows better deoxygenation reactivity than Pd/SBA-15-spherelike catalyst. Exceptionally high conversion of 70< technical grade of methyl oleate into diesel fuel aliphatic hydrocarbons (C15 – C18) is achieved at mild temperature i.e. 270°C and high H2 pressure, 60 bar in 6 h reaction time using batch reactor. Indirect decarbonylation pathway is dominant as increasing of reaction time. Here is found that Pd/SBA-15 is keenly involved in methanation during reaction progression. Deoxygenation of methyl oleate, surrogate molecule of vegetable oil, in the present work is greatly influenced by different support morphologies and reaction parameters.
Necklacelike mesoporous SBA-15 was prepared by dissolving Pluronic P123 (PEO20PPO70PEO20) (Aldrich) in 2 M hydrochloric acid (HCl) (Merck) at 35°C before addition of tetraethylorthosilicate (TEOS) (Merck). The reaction mixture was then continuously stirred at 35°C for 24 h. Next, the solution temperature was raised to 80°C and stirred another 48 h. Meanwhile, spherelike SBA-15 was prepared by vigorously stirring the reaction mixture at 35°C for 10 minutes. Subsequently, the solution mixture was kept in isothermally static condition for 6 h. Template removal of SBA-15 was achieved by calcination in air at 550°C for 4 h. SBA-15 supported palladium catalyst, Pd/SBA-15 with 3.8 wt< Pd was prepared by impregnation method, filtered, air dried and calcination in air at 550°C for 4 h.
The concentration of Pd (wt<) incorporated into SBA-15 was measured by Inductively Coupled Plasma-Mass Spectrometer (ICP-MS), Agilent 7500 series. The BET surface area and pore diameters of the samples were determined by nitrogen adsorption-desorption isotherms measurement at 77 K using Quantachrome Autosorb 6B. XRD patterns of the catalysts were recorded with Bruker AXS D8 Discover equipped with general area diffraction detector system (GADDS) working with CoKα1 (1.5418 Å). In order to obtain higher solution of low angle XRD patterns, all the calcined samples were recorded on Bruker D8 Advance Powder diffractormeter (CuKα1 radiation, λ = 1.5406 Å).
The metal dispersion of supported palladium catalysts were investigated by H2 chemisorption. Pulse chemisorption on reduced palladium catalysts was performed at 70°C using Temperature Programmed Desorption Reduction and Oxidation (TPDRO) 1100 (Thermo Finnigan). The number of exposed palladium atoms on the surface was calculated by the total amount of hydrogen adsorped using the molar ratio between Pd:H2 as 0.5 .
FESEM coupled with EDX analysis was performed on Supra 55 VP, Carl Zeiss scanning electron microscopy. Low accelerating voltage FESEM image of the catalysts were taken using Hitachi SU-8000.
Transmission Electron Microscope (TEM) micrographs were captured by Carl Zeiss LIBRA 200 (with an accelerating voltage 200 kV).
Evaluation of the Pd/SBA-15 performance in deoxygenation reaction was carried out in a 200 ml Hastelloy autoclave. The catalysts were primarily reduced with 5 vol< H2/Ar at 300°C for 1 h while, the autoclave was charged with 10 wt< of model feedstock, methyl oleate (70< Aldrich) in n-heptane. Then, the active catalysts were charged in the reactor vessel under inert atmosphere and the reaction was conducted at temperature between 250 – 300°C and H2 pressure range from 25 to 80 bar. Liquid reaction samples were analyzed offline using gas chromatography coupled with mass spectrometer (Shimadzu QP5050) using HP-5 column. Gas samples were taken out from the autoclave in a 100 ml gas tank and injected with a gas syringe on a gas chromatography (Agilent, 7890A) equipped with a thermal conductivity detector (TCD), split/splitless injection system and Porapak Q column.
The financial support from Universiti Teknologi PETRONAS under STIRF grant (82/09.10) is gratefully acknowledged.
- Gunter A, Irion WW, Nevwirth OS: Oil refining. Handbook of fuels. Edited by: Elvers B. 2008, Germany: WILEY-VCH Verlag GmbH & Co. KGaA Weinhem, 17-95.Google Scholar
- Secretariat for the United Nations Framework Convention on Climate Change: Kyoto protocol to the United Nation Framework Convention on Climate Change. UN Doc FCCC/CP/1997/7/Add.1, Dec. 10, 1997; 37 ILM 22 1998. Available from: http://unfccc.int/essential_background/kyoto_protocol/background/items/1351.php
- Jos GJ O, Greet J-M, Jeroen AHW P, Julian W: Long-term trend in global CO2 emissions 2011 report background studies. 2011, Hague: PBL Netherlands Environmental Assessment Agency, 1-42. 500253004.Google Scholar
- Chen S, Yokoi T, Tamg C, Jang L, Tatsumi T, Chan JCC, Cheng S: Sulfonic acid-functionalized platelet SBA-15 materials as efficient catalysts for biodiesel synthesis. Green Chem. 2011, 13: 2920-2930. 10.1039/c1gc15299h.View ArticleGoogle Scholar
- Vasudevan PT, Briggs M: Biodiesel production – current state of the art and challenges. J Ind Microbiol Biotechnol. 2008, 35: 421-430. 10.1007/s10295-008-0312-2.View ArticleGoogle Scholar
- Bezergianni S, Kalogianni A: Hydrocracking of used cooking oil for biofuels production. Bioresour Technol. 2009, 100: 3927-3932. 10.1016/j.biortech.2009.03.039.View ArticleGoogle Scholar
- Bezergianni S, Voutetakis S, Kalogianni A: Catalytic hydrocracking of fresh and used cooking oil. Ind & Eng Chem Res. 2009, 48: 8402-8406. 10.1021/ie900445m.View ArticleGoogle Scholar
- Boda L, Onyestyak G, Solt H, Lonyi F, Valyon J, Thernesz A: Catalytic hydroconversion of tricaprylin and caprylic acid as model reaction for biofuel production from triglycerides. Appl Catal A. 2010, 374: 158-169. 10.1016/j.apcata.2009.12.005.View ArticleGoogle Scholar
- Choudhary TV, Philips CB: Renewable fuels via catalytic hydrodeoxygenation. Appl Catal A. 2011, 397: 1-12. 10.1016/j.apcata.2011.02.025.View ArticleGoogle Scholar
- Donnis B, Egeberg RG, Blom P, Knudsen KG: Hydroprocessing of bio-oils and oxygenates to hydrocarbons understanding the reaction. Top Catal. 2009, 52: 229-240. 10.1007/s11244-008-9159-z.View ArticleGoogle Scholar
- Lestari S, Maki-Arvela P, Bernas H, Simakova O, Sjoholm R, Beltramini J, Lu GQM, Mylloyoja J, Simakova I, Murzin DY: Catalytic deoxygenation stearic acid in continuous reactor over a mesoporous carbon-supported Pd catalyst. Energy Fuel. 2009, 23: 3842-3845. 10.1021/ef900110t.View ArticleGoogle Scholar
- Knothe G: Biodiesel and renewable diesel: a comparison. Progress in Energy and Comb Sci. 2010, 36: 364-373. 10.1016/j.pecs.2009.11.004.View ArticleGoogle Scholar
- Kubicka D, Bejblova M, Vlk J: Covnversion of vegetable oils into hydrocarbons over CoMo/MCM-41 Catalysts. Top Catal. 2010, 53: 168-179. 10.1007/s11244-009-9421-z.View ArticleGoogle Scholar
- Kwon KC, Mayfield H, Marolla T, Nichols B, Mashburn M: Catalytic deoxygenation of liquid biomass for hydrocarbon fuels. Renew Energy. 2011, 36: 907-915. 10.1016/j.renene.2010.09.004.View ArticleGoogle Scholar
- Senol OI, Viljaya T-R, Krause AOI: Hydrodeoxygenation of methyl esters on sulphided NiMo/γ-Al2O3 and CoMo/γ-Al2O3. Catal Today. 2005, 100: 331-335. 10.1016/j.cattod.2004.10.021.View ArticleGoogle Scholar
- Yang Y, Ochoa-Hernandez C, O’Shea V, de la Pena A, Coronado JM, Serrano DP: Ni2P/SBA-15 as a hydrodeoxygenation catalyst with enhanced selectivity for the conversion of methyl oleate into n-octadecane. ACS Catal. 2012, 2: 592-598. 10.1021/cs200659r.View ArticleGoogle Scholar
- Huber GW, Iborra S, Corma A: Synthesis of transportation fuels from biomass: chemistry, catalysts, and engineering. Chem Rev. 2006, 2: 40044-4098.Google Scholar
- Kubickova I, Kubicka D: Utilization of triglycerides and related feedstocks for production of clean hydrocarbon fuels and petrochemicals. Waste and Biomass Volarization. 2010, 1: 293-308. 10.1007/s12649-010-9032-8.View ArticleGoogle Scholar
- Snare M, Kubickova I, Maki-Arvela P, Eranen K, Murzin DY: Heterogeneous catalytic deoxygenation of stearic acid for production of biodiesel. Ind & Eng Chem Res. 2006, 45: 5708-5715. 10.1021/ie060334i.View ArticleGoogle Scholar
- Simakova I, Simakova O, Maki-Arvela P, Simakova A, Estrada M, Murzin DY: Deoxygenation of palmitic and stearic acid over supported Pd catalysts: effect of metal dispersion. Appl Catal A. 2009, 355: 100-108. 10.1016/j.apcata.2008.12.001.View ArticleGoogle Scholar
- Snare M, Kubickova I, Maki-Arvela P, Chichova D, Eranen K, Murzin DY: Catalytic deoxygenation of unsaturated renewable feedstocks for production of diesel fuel hydrocarbons. Fuel. 2008, 87: 933-945. 10.1016/j.fuel.2007.06.006.View ArticleGoogle Scholar
- Lestari S, Maki-Arvela P, Simakova I, Beltramini J, Lu GQM, Murzin DY: Catalytic deoxygenation of stearic acid and palmitic acid. Catal Lett. 2009, 130: 48-51. 10.1007/s10562-009-9889-y.View ArticleGoogle Scholar
- Kubickova I, Snare M, Eranen K, Maki-Arvela P, Murzin DY: Hydrocarbons for diesel fuel via decarboxylation of vegetable oil. Catal Today. 2005, 106: 197-200. 10.1016/j.cattod.2005.07.188.View ArticleGoogle Scholar
- Simakova I, Simakova O, Maki-Arvela P, Murzin DY: Decarboxylation of fatty acids over Pd supported on mesoporous carbon. Catal Today. 2010, 150: 28-31. 10.1016/j.cattod.2009.07.064.View ArticleGoogle Scholar
- Madsen AT, Ahmed EH, Christensen CH, Fehrmann R, Riisager A: Hydrodeoxygenation of waste fat for diesel production: study on model feed with Pt/alumina catalyst. Fuel. 2011, 90: 3433-3438. 10.1016/j.fuel.2011.06.005.View ArticleGoogle Scholar
- Immer JG, Lamb HH: Fed-batch catalytic deoxygenation of free fatty acids. Energy Fuel. 2010, 24: 5291-5299. 10.1021/ef100576z.View ArticleGoogle Scholar
- Ping EW, Wallace R, Pierson J, Fuller TF, Jones CW: Highly dispersed palladium nanoparticles on ultra-porous silica mesocellular foam for the catalytic decarboxylation of stearic acid. Microporous Mesoporous Mater. 2010, 132: 174-180. 10.1016/j.micromeso.2010.02.017.View ArticleGoogle Scholar
- Zhao D, Feng J, Huo Q, Melosh N, Fredrickson G, Chmelka B, Stucky G: Triblock copolymer syntheses of mesoporous silica with periodic 50 to 300 angstrom pores. Sci. 1998, 279: 548-552. 10.1126/science.279.5350.548.View ArticleGoogle Scholar
- Yuranov I, Moeckli P, Suvorova E, Buffat P, Kiwi-Minsker L, Renken A: Pd/SiO2 catalysts: synthesis of Pd nanoparticles with the controlled size in mesoporous silicas. J of Mol Cat A. 2003, 192: 239-251. 10.1016/S1381-1169(02)00441-7.View ArticleGoogle Scholar
- Chen L-F, Guo P-J, Zhu L-J, Qiao M-H, Shen W, Xu H-L: Preparation of Cu/SBA-15 catalysts by different methods for the hydrogenolysis of dimethyl maleate to 1,4-butanediol. Appl Catal A. 2009, 356: 129-136. 10.1016/j.apcata.2008.12.029.View ArticleGoogle Scholar
- He C, Zhang F, Yue L, Shang X, Chen J, Hao Z: Nanometric palladium confined in mesoporous silica as efficient catalyst for toluene oxidation at low temperature. Appl Catal B. 2011, 111 (112): 46-57.Google Scholar
- Kosuge K, Sato T, Kikukawa N, Takemori M: Morphological control of rod- and fiberlike SBA-15 type mesoporous silica using water-soluble sodium silicate. Chem Of Mater. 2004, 16: 899-905. 10.1021/cm030622u.View ArticleGoogle Scholar
- Han P, Wang X, Qiu X, Ji X, Gao L: One step synthesis of palladium/SBA-15 nanocomposites and its catalytic application. J of Mol Catal A. 2007, 272: 136-141. 10.1016/j.molcata.2007.03.006.View ArticleGoogle Scholar
- Naskar MK, Eswaramoorthy M: Significant improvement in the pore properties of SBA-15 brought about by carboxylic acids and hydrothermal treatment. J Chem Sci. 2008, 120: 181-186. 10.1007/s12039-008-0021-4.View ArticleGoogle Scholar
- Galarneau A, Cambon H, Renzo FD, Ryoo R, Choi M, Fajula F: Microporosity and connections between pores in SBA-15 mesostructured silicas as a function of the temperature of synthesis. New J Chem. 2003, 27: 73-79. 10.1039/b207378c.View ArticleGoogle Scholar
- Naik B, Ghosh NN: A review on chemical methodologies for preparation of mesoporous silica and alumina based materials. Recent Pat Nanotechnol. 2009, 3: 213-224. 10.2174/187221009789177768.View ArticleGoogle Scholar
- Galarneau A, Cambon H, Renzo FD, Fajula F: True microporosity and surface area of mesoporous SBA-15 silicas as a function of synthesis temperature. Langmuir. 2001, 17: 8328-8335. 10.1021/la0105477.View ArticleGoogle Scholar
- Guo W, Park J, Oh M, Jeong H, Cho W, Kim I: Triblock copolymer synthesis of highly ordered large-pore periodic mesoporous organosilicas with the aid of inorganic salts much progress has been made recently in the prepa- ration of a new class of organic–inorganic hybrid materials called periodic meso. Chem Mater. 2003, 15: 2295-2298. 10.1021/cm0258023.View ArticleGoogle Scholar
- Chao M-C, Chang C-H, Lin H-P, Tang C-Y, Lin C-Y: Morphological control on SBA-15 mesoporous silica via a slow self-assembling rate. J Mater Sci. 2009, 44: 6453-6462. 10.1007/s10853-009-3610-9.View ArticleGoogle Scholar
- Kosuge K, Kubo S, Kikukawa N, Takemori M: Effect of pore structure in mesoporous silicas on VOC dynamic adsorption/desorption performance. Langmuir. 2007, 23: 3095-3102. 10.1021/la062616t.View ArticleGoogle Scholar
- Wang P, Wang Z, Li J, Bai Y: Preparation, characterizations, and catalytic characteristics of Pd nanoparticles encapsulated in mesoporous silica. Microporous Mesporous Mater. 2008, 116: 400-405. 10.1016/j.micromeso.2008.04.029.View ArticleGoogle Scholar
- Lestari S, Maki-Arvela P, Eranen K, Beltramini J, Max Lu GQ, Murzin DY: Diesel-like hydrocarbons from catalytic deoxygenation of stearic acid over supported Pd nanoparticles on SBA-15 catalysts. Catal Lett. 2009, 134: 250-257.View ArticleGoogle Scholar
- Anita R, Lee S-P: Short term internal research report. Catalytic deoxygneation of methyl oleate with supported Pd on SBA-15. 2012, Malaysia: Universiti Teknologi PETRONASGoogle Scholar
- Yueping K, Nongyue H, Jian W, Pengfeng X, Chuwei Y, Zuhong L: Investigating the state of Fe and La in MCM-41 mesoporous molecular sieve materials. Colloids Surf A. 2001, 179: 177-184. 10.1016/S0927-7757(00)00654-3.View ArticleGoogle Scholar
- Bendahou K, Cherif L, Siffert S, Tidahy HL, Benaissa H, Aboukais A: The effect of the use of lanthanum-doped mesoporous SBA-15 on the performance of Pt/SBA-15 and Pd/SBA-15 catalysts for total oxidation of toluene. Appl Catal A. 2008, 351: 82-87. 10.1016/j.apcata.2008.09.001.View ArticleGoogle Scholar
- Ghasem RB, Reihaneh M, Fereshteh J, Zeinab P, Hassan A: Covalent anchoring of copper-Schiff complex into SBA-15 as a heterogeneous catalyst for the synthesis of pyridopyrazine and quinoxaline derivatives. Catal Commun. 2012, 27: 49-53.View ArticleGoogle Scholar
- Simacek P, Kubicka D, Sebor G, Pospisil M: Hydroprocessed rapeseed oil as a source of hydrocarbon-based biodiesel. Fuel. 2009, 88: 456-460. 10.1016/j.fuel.2008.10.022.View ArticleGoogle Scholar
This article is published under license to BioMed Central Ltd. This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.