Synthesis and characterization of new polyamides derived from alanine and valine derivatives

Chemistry Central Journal volume 6, Article number: 128 (2012) Cite this article

Abstract

Background

Many efforts have been recently devoted to design, investigate and synthesize biocompatible, biodegradable polymers for applications in medicine for either the fabrication of biodegradable devices or as drug delivery systems. Many of them consist of condensation of polymers having incorporated peptide linkages susceptible to enzymatic cleavage. Polyamides (PAs) containing α-amino acid residues such as L-leucine, L-alanine and L-phenylalanine have been reported as biodegradable materials. Furthermore, polyamides (PAs) derived from C10 and C14 dicarboxylic acids and amide-diamines derived from 1,6-hexanediamine or 1,12-dodecanediamine and L-phenylalanine, L-valyl-L-phenylalanine or L-phenylalanyl-L-valine residues have been reported as biocompatible polymers. We have previously described the synthesis and thermal properties of a new type of polyamides-containing amino acids based on eight new symmetric meta-oriented protected diamines derived from coupling of amino acids namely; Fomc-glycine, Fmoc-alanine, Fomc-valine and Fomc-leucine with m-phenylene diamine or 2,6-diaminopyridine. Results revealed that incorporation of pyridine onto the polymeric backbone of all series decreases the thermal stability.

Here we describe another family of polyamides based on benzene dicarboxylic acid, pyridine dicarboxylic acid, and α-amino acid linked to benzidine and 4,4′-oxydianiline to study the effect of the dicarboxylic acid as well as the amino acids on the nature and thermal stability of the polymers.

Results

We report here the preparation of a new type of polyamides based on benzene dicarboxylic acid, pyridine dicarboxylic acid, and α-amino acid linked to benzidine and 4,4′-oxydianiline to study the effect of the dicarboxylic acid as well as the amino acids on the nature and thermal stability of polymers. The thermal properties of the polymers were evaluated by different techniques. Results revealed that structure-thermal property correlation based on changing the dicarboxylic acid monomer or the diamine monomer demonstrated an interesting connection between a single change (changing the dicarboxylic acids in each series while the diamine is fixed) and thermal properties. The newly prepared polymers may possess biodegradability and thus may find some applications as novel biomaterials.

Conclusions

The thermal properties of the new type of polyamides based on benzene dicarboxylic acid, pyridine dicarboxylic acid, and α-amino acid (alanine and valine) linked to benzidine and 4,4′-oxydianiline were evaluated by thermal gravimetric (TG), differential thermal gravimetric (DTG) and differential thermal analysis (DTA) techniques. Results revealed that the structure-thermal property correlation based on changing the dicarboxylic acid monomer or the diamine monomer demonstrated an interesting connection between a single change (changing the dicarboxylic acids in each series while the diamine is fixed) and thermal properties. In addition, pyridine-containing polymers exhibited semicrystalline characteristic with melting temperature, T m . where none of the valine-containing polymers showed a melting and crystallization peak indicating that the polymers were amorphous. This is expected since L-valine side chain can inhibit close packing and eliminate crystallization. The newly prepared polymers may possess biodegradability and thus may find some applications as novel biomaterials.

Background

Many efforts have been recently devoted to design, investigate and synthesize biocompatible, biodegradable polymers for applications in medicine for either the fabrication of biodegradable devices or as drug delivery systems [1–5]. Many of them consist of condensation polymers having incorporated peptide linkages susceptible to enzymatic cleavage. Polyamides (PAs) containing α-amino acid residues such as L-leucine, L-alanine and L-phenylalanine have been reported as biodegradable materials [6, 7]. Jin et al. [8] prepared polyamides, and polyureas containing L-leucine and L-tyrosine residues in the chain. Polyester amides derived from α-amino acids and α-hydroxyacids, the polydepsipeptides, have also been investigated as biodegradable polymers [9, 10]. Polyamides (PAs) derived from C10 and C14 dicarboxylic acids and amide-diamines derived from 1,6-hexanediamine or 1,12-dodecanediamine and L-phenylalanine, L-valyl-L-phenylalanine or L-phenylalanyl-L-valine residues have been reported as a biocompatible polymers [11–13]. Furthermore, an appropriate choice of the number and sequence of the α-amino acids, as well as a balance of hydrophilic and hydrophobic characteristics of the other constituents, makes these polymers susceptible to enzymatic cleavage of the peptide bonds by specific enzymes [6, 14–19].

Diamine type monomers derived from glycine [20], (D, L)- and (L)-alanine [21–30], (D, L)- and (L)-phenylalanine [31, 32] and various aliphatic diols or from tyrosine–leucine-dipeptide [19, 33] and different diamines, were utilized to obtain the polyester amides or polyamides. In general, it is expected that derivatives of L-alanine could be highly crystalline with extensive hydrogen bonding in contrast to the amorphous character of polymers that could be synthesized from α-amino acids with bulky side groups [8, 34, 35].

We have previously [36] described the synthesis and thermal properties of a new type of polyamides-containing amino acids based on eight new symmetric meta-oriented protected diamines derived from coupling of four types of Fmoc-amino acids namely; Fomc-glycine, Fmoc-alanine, Fomc-valine and Fomc-leucine with m-phenylene diamine or 2,6-diaminopyridine. Results revealed that incorporation of pyridine onto the polymeric backbone of all series decreases the thermal stability [36].

Here we describe another family of polyamides based of benzene dicarboxylic acid, pyridine dicarboxylic acid, and α-amino acid linked to benzidine and 4,4′-oxydianiline to study the effect of the dicarboxylic acid as well as the amino acids on the nature and thermal stability of the polymer.

Experimental

Materials and methods

The solvents used were of HPLC reagent grade. The commercial isophthalic acid (Merck), pyridine-2,6-dicarboxylic acid (Aldrich), pyridine-3,5-dicarboxylic acid (Aldrich), Fmoc-amino acids namely Fmoc-Ala-OH 1, Fmoc-Val-OH 2, and (O-(7-azabenzotriazol-1-yl)-1,1,3,3-tetramethyluronium hexafluorophosphate) (HATU) (IRIS Biotech, Germany), benzidine (Aldrich) 3, 4,4′-oxydianiline (Aldrich) 4 and the solvents triethylamine (Et3N), N,N-dimethylacetamide (DMAc), N,N-dimethylformamide (DMF), 1-Methyl-2-pyrrolidone (NMP) (Fluka), diethylamine, acetonitrile, chloroform, n-hexane, ethyl alcohol were used as purchased without purification.

Melting points were determined with a Mel-Temp apparatus and are uncorrected. Infrared spectra (IR) were recorded on a FTIR-8400S Shimadzu-Japan or on a Perkin-Elmer 1600 series, Fourier transform instrument as KBr pellets. Absorption spectra were measured with a UV 500 UV–vis spectrometer at room temperature (rt) in DMSO with a polymer concentration of 1 mg/10 mL. Magnetic resonance spectra (1H NMR and 13C NMR spectra) were recorded on a JEOL 500 MHz spectrometer with chemical shift values reported in δ units (ppm) relative to an internal standard. Follow-up of the reactions and checks of the purity of the compounds was done by thin layer chromatography (TLC) on silica gel-protected aluminum sheets (Type 60 GF254, Merck) and the spots were detected by exposure to UV-lamp at λ 254 nm for a few seconds. Differential thermogravimetric (DTG) analyses were carried out in the temperature range from 20°C to 500°C in a steam of nitrogen atmosphere by Shimadzu DTG 60H thermal analyzer. The experimental conditions were: platinum crucible, nitrogen atmosphere with a 30 ml/min flow rate and a heating rate 10°C/min. Differential thermal analysis (TGA/DTA) analyses were carried out using SDT-Q600-V20.5-Build at the Institute of Graduate Studies and Research, Alexandria University and at the Microanalysis Center, Cairo University, Giza, Egypt. Elemental analyses were performed at the Microanalytical Unit, Cairo University and Center for mycology and biotechnology, Alazhar University, Cairo.

Synthesis of Bis Fmoc-protected diamines 5–8 (general method)

To a solution of Fmoc–Ala-OH 1 (0.623 g, 2 mmol) or Fmoc–Val-OH 2 (0.679 g, 2 mmol); diisopropylethylamine (DIEA, 0.7 mL, 4 mmol) in 5 mL DMF was added HATU (0.76 g, 2 mmol) as a coupling reagent. The reaction mixture was stirred for 3 min (to preactivate the carboxylic acid and form the N-protect amino acid active ester), followed by the addition of a solution of diamine 3 (0.2 g, 1 mmol) or 4 (0.184 g, 1 mmol) in 2 ml DMF. The reaction mixture was stirred overnight and then was poured over water. The precipitate was filtered, washed with 5% citric acid (3 × 20 mL), saturated NaHCO3 (3 × 20 mL) and water. The crude product was recrystallized from CH2Cl2/hexane.

Bis((9H-fluoren-9-yl)methyl) 1,1′-(biphenyl-4,4′-diylbis(azanediyl))bis(1-oxopropane-2,1-diyl)dicarbamate 5 (FT-IR, 1H NMR and 13C NMR are attached as supporting information; Additional files 1, 2, 3respectively)

The reaction of Fmoc-Ala-OH 1 with benzidine 3 gave compound 5. The product was obtained as a white powder, mp 158-159°C, in yield 0.65 g (84%). IR (KBr): 3301 (NH), 1671 (C=O, amide) cm-1. 1H-NMR (CDCl3, 500Hz): δ 1.23-1.30 (m, 6H, 2 CH3), 4.18-4.24 (m, 4H, 4 CH), 6.24 (s, 4H, 2 CH2), 6.82, 6.92 (2brs, 2H, 2 NH, D2O exchangeable), 7.31-7.86 (m, 24H, Ar-H), 10.11, 10.13 (2s, 2H, 2 NH, D2O exchangeable). 13C-NMR (CDCl3, 125Hz): δ 21.82, 51.41, 110.34, 120.16, 120.54, 121.90, 126.95, 127.90, 129.53, 134.99, 137.88, 138.39, 139.87, 143.00, 154.00, 175.60. Anal. Calcd for C48H42N4O6: C, 74.79; H, 5.49; N, 7.27. Found: C, 75.02; H, 5.77; N, 6.95.

Bis((9H-fluoren-9-yl)methyl)-1,1′-(biphenyl-4,4′-diylbis(azanediyl))bis(3-methyl-1-oxobutane-2,1-diyl) dicarbamate 6 (FT-IR, 1H NMR and 13C NMR are attached as supporting information; Additional files 4, 5, 6respectively)

The reaction of Fmoc-Val-OH 2 with benzidine 3 gave compound 6. The product was obtained as a white powder, mp 212-213°C, in yield 0.77 g (93%). IR (KBr): 3289 (NH), 1692, 1660 (C=O, amide) cm-1. 1H-NMR (CDCl3, 500Hz): δ 0.82, 0.89 (2d, 12H, J= 6.9 Hz, 4 CH3), 1.86-1.90 (m, 2H, 2 CH), 3.08 (d, 2H, J = 6.1 Hz, 2 CH), 3.77-3.81 (m, 2H, 2 CH), 6.24 (s, 4H, 2 CH2), 7.30, 7.38 (2t, 8H, J = 7.6 Hz, Ar-H), 7.51-7.56 (m, 5H, NH+ Ar-H), 7.64-7.69 (m, 5H, NH+ Ar-H), 7.80, 7.84 (2d, 8H, J = 7.6 Hz, Ar-H), 9.95, 10.45 (2brs, 2H, 2 NH, D2O exchangeable). 13C-NMR (CDCl3, 125Hz): δ 17.84, 18.99, 19.94, 20.02, 20.15, 61.33, 110.34, 120.08, 120.57, 121.93, 126.96, 127.84, 129.47, 137.94, 139.93, 143.08, 174.50. Anal. Calcd for C52H50N4O6: C, 75.52; H, 6.09; N, 6.77. Found: C, 75.36; H, 5.95; N, 6.51.

Bis((9H-fluoren-9-yl)methyl)-1,1′-(4,4′-oxybis(4,1-phenylene)bis(azanediyl))bis(1-oxopropane-2,1-diyl)dicarbamate 7 (FT-IR, 1H NMR and 13C NMR are attached as supporting information; Additional files 7, 8, 9respectively)

The reaction of Fmoc-Ala-OH 1 with 4,4′-oxydianiline 4 gave compound 7. The product was obtained as a white powder, mp 133-134°C, in yield 0.66 g (84%). IR (KBr): 3452, 3288 (NH), 1668 (C=O, amide) cm-1. 1H-NMR (CDCl3, 500Hz): δ 1.27 (d, 6H, 2 CH3), 4.18-4.24 (m, 8H, 4 CH+ 2 CH2), 6.90 (d, 4H, Ar-H), 7.27-7.32 (m, 4H, Ar-H), 7.38 (t, 4H, Ar-H), 7.56 (d, 4H, Ar-H), 7.65 (d, 1H, NH, D2O exchangeable), 7.71 (t, 4H, Ar-H), 7.80 (d, 1H, NH, D2O exchangeable), 7.85 (d, 4H, Ar-H), 9.99 (s, 2H, 2 NH, D2O exchangeable). 13C-NMR (CDCl3, 125Hz): δ 21.66, 51.17, 110.31, 119.22, 120.50, 121.67, 121.87, 127.94, 129.57, 134.63, 137.83, 139.82, 142.93, 153.15, 175.46. Anal. Calcd for C48H42N4O7: C, 73.27; H, 5.38; N, 7.12. Found: C, 73.64; H, 5.09; N, 6.87.

Bis((9H-fluoren-9-yl)methyl)-1,1′-(4,4′-oxybis(4,1-phenylene)bis(azanediyl))bis(3-methyl-1-oxobutane-2,1-diyl)dicarbamate 8 (FT-IR, 1H NMR and 13C NMR are attached as supporting information; Additional files 10, 11, 12respectively)

The reaction of Fmoc-Val-OH 2 with 4,4′-oxydianiline 4 gave compound 8. The product was obtained as a white powder, mp 193-194°C, in yield 0.75 g (89%). IR (KBr): 3292 (NH), 1691, 1660 (C=O, amide) cm-1. 1H-NMR (CDCl3, 500Hz): δ 0.80, 0.87 (2d, 12H, J= 6.9 Hz, 4 CH3), 1.84-1.90 (m, 2H, 2 CH), 3.04 (d, 2H, J = 5.4 Hz, 2 CH), 6.24 (s, 4H, 2 CH2), 6.90 (d, 4H, J= 8.4 Hz, Ar-H), 7.30, 7.38 (2t, 8H, J= 7.6 Hz, Ar-H), 7.50-7.58 (m, 2H, 2 NH, D2O exchangeable), 7.60 (d, 4H, J= 8.4 Hz, Ar-H), 7.80, 7.84 (2d, 8H, J= 7.6 Hz, Ar-H), 9.83, 10.47 (2brs, 2H, 2 NH, D2O exchangeable). 13C-NMR (CDCl3, 125Hz): δ 17.85, 20.16, 31.10, 61.27, 110.36, 119.18, 120.57, 121.34, 121.93, 127.83, 129.46, 134.98, 137.94, 139.94, 143.08, 152.99, 174.29. Anal. Calcd for C52H50N4O7: C, 74.09; H, 5.98; N, 6.65. Found: C, 73.87; H, 5.53; N, 6.21.

General procedure for the deblocking of the Fmoc-protecting groups: preparation of the diamines 9–12

Protected diamine (0.5 mmol) 5–8 was stirred with 40 ml (30% Et2NH / CH3CN) at r.t. for 14h. The progress of the reaction was monitored by using TLC using ethyl acetate / hexane 4:6 v/v as eluent. The solvent and volatiles were removed under reduced pressure and the crude residue was washed thoroughly with hexane to get rid from the deblocked dibenzofulvene byproduct to produce the desired diamine 9–12 which is used directly to the next step.

Preparation of polymers 16–25 by low-temperature solution polycondensation (general method)

To a mechanically stirred cold (ice bath) solution of the diamine 9–12 (1.0 mmol) dissolved in 5.0 mL DMA, a solution of 1.0 mmol of the acid dichloride 13, 14, 15 dissolved in 5.0 mL DMA was added dropwise. The reaction mixture was allowed to stir for 2h then the mixture was poured into iced water. The formed polymer precipitate was filtered under vacuum, washed thoroughly with water, ethyl alcohol and water again, dried and kept in the desiccator.

Poly[3-acetyl-N-((2S)-1-(4′-(2-(methylamino)propanamido)biphenyl-4-ylamino)-1-oxopropan-2-yl)benzamide] 16

The polymerization of the diamine 9 with isophthaloyl dichloride 13 produced the polymer 16 as a black solid, yield 59.0%, m. p. > 300°C, UV (DMSO): λmax= 272 nm (ε =1569), λmax= 304 nm (ε =1684), IR (cm-1): 3230 (N-H, amide), 3064 (=C–H, aromatic), 2921 (C–H, aliphatic), 1658 (C=O, amide), 1599 and 1497 (C=C, aromatic), 1114 and 1071 (C–N, aliphatic). Calculated for C26H26N4O5; C, 65.81; H, 5.52; N, 11.81; Found: C, 65.52; H, 5.78; N, 11.55.

Poly[3-acetyl-N-((2S)-3-methyl-1-(4′-(3-methyl-2-(methylamino) butanamido)biphenyl-4-ylamino)-1-oxobutan-2-yl)benzamide] 17

The polymerization of the diamine 10 with isophthaloyl dichloride 13 produced the polymer 17 as a black solid, yield 56.0%, m. p. > 300°C, UV (DMSO): λmax= 275 nm (ε =2244), λmax= 300 nm (ε =2156), IR (cm-1): 3430 (N-H, amide), 3039 (=C–H, aromatic), 2921 (C–H, aliphatic), 1658 (C=O, amide), 1607 and 1446 (C=C, aromatic), 1249 and 1113 (C–N, aliphatic). Calculated for C30H34N4O5; C, 67.91; H, 6.46; N, 10.56; Found: C, 67.72; H, 6.70; N, 10.77.

Poly[3-acetyl-N-((2S)-1-(4-(4-(2-(methylamino)propanamido)phenoxy) phenylamino)-1-oxopropan-2-yl)benzamide] 18

The polymerization of the diamine 11 with isophthaloyl dichloride 13 produced the polymer 18 as a black solid, yield 68.0%, m. p. > 300°C, UV (DMSO): λmax= 268 nm (ε =1359), λmax= 276 nm (ε =1169), λmax= 362 nm (ε = 86), IR (cm-1): 3439 (N-H, amide), 3096 (=C–H, aromatic), 2935 (C–H, aliphatic), 1669 (C=O, amide), 1592 and 1490 (C=C, aromatic), 1114 and 1070 (C–N , aliphatic). Calculated for C26H26N4O6; C, 63.66; H, 5.34; N, 11.42; Found: C, 63.29; H, 5.08; N, 11.73.

Poly[3-acetyl-N-((2S)-3-methyl-1-(4-(4-(3-methyl-2-(methylamino)butanamido) phenoxy)phenylamino)-1-oxobutan-2-yl)benzamide] 19

The polymerization of the diamine 12 with isophthaloyl dichloride 13 produced the polymer 19 as a black solid, yield 60.0%, m. p. > 300°C, UV (DMSO): λmax= 268 nm (ε =1754), λmax= 330 nm (ε =158), IR (cm-1): 3477 (N-H, amide), 3036 (=C–H, aromatic), 2887 (C–H, aliphatic), 1640 (C=O, amide), 1610 and 1475 (C=C, aromatic), 1216 and 1150 (C–N, aliphatic). Calculated for C30H34N4O6; C, 65.92; H, 6.27; N, 10.25; Found: C, 66.28; H, 6.61; N, 10.60.

Poly[6-acetyl-N-((2S)-1-(4′-(2-(methylamino)propanamido)biphenyl-4-ylamino)-1-oxo propan-2-yl)picolinamide] 20

The polymerization of the diamine 9 with pyridine-2,6-dicarbonyl dichloride 14 produced the polymer 20 as a black solid, yield 56.0%, m. p. > 300°C, UV (DMSO): λmax= 268 nm (ε =1930), λmax= 321 nm (ε =459), IR (cm-1): 3400 (N-H, amide), 3063 (=C–H, aromatic), 2934 (C–H, aliphatic), 1668 (C=O, amide), 1590 and 1489 (C=C, aromatic), 1440 (C–N , aromatic), 1113 and 1070 (C–N, aliphatic). Calculated for C25H25N5O5; C, 63.15; H, 5.30; N, 14.73; Found: C, 63.41; H, 5.06; N, 14.61.

Poly[6-acetyl-N-((2S)-3-methyl-1-(4′-(3-methyl-2-(methylamino) butanamido)biphenyl-4-ylamino)-1-oxobutan-2-yl)picolinamide] 21

The polymerization of the diamine 10 with pyridine-2,6-dicarbonyl dichloride 14 produced the polymer 21 as a black solid, yield 62.0%, m. p. > 300°C, UV (DMSO): λmax= 275 nm (ε = 2162), λmax= 299 nm (ε =2106), IR (cm-1): 3416 (N-H, amide), 3039 (=C–H, aromatic), 2890 (C–H, aliphatic), 1642 (C=O, amide), 1613 and 1477 (C=C, aromatic), 1445 (C–N , aromatic), 1215 and 1150 (C–N , aliphatic). Calculated for C29H33N5O5; C, 65.52; H, 6.26; N, 13.17 Found: C, 65.85; H, 5.96; N, 12.89.

Poly[6-acetyl-N-((2S)-1-(4-(4-(2-(methylamino)propanamido)phenoxy) phenylamino)-1-oxopropan-2-yl)picolinamide] 22

The polymerization of the diamine 11 with pyridine-2,6-dicarbonyl dichloride 14 produced the polymer 22 as a black solid, yield 58.0%, m. p. > 300°C, UV (DMSO): λmax= 268 nm (ε = 767), λmax= 276 nm (ε =651), IR (cm-1): 3440 (N-H, amide), 3096 (=C–H, aromatic), 2936 (C–H, aliphatic), 1692 (C=O, amide), 1591 and 1490 (C=C, aromatic), 1441 (C–N , aromatic), 1113 and 1070 (C–N , aliphatic). Calculated for C25H25N5O6; C, 61.09; H, 5.13; N, 14.25 Found: C, 61.32; H, 5.44; N, 13.98.

Poly[5-acetyl-N-((2S)-1-(4′-(2-(methylamino)propanamido)biphenyl-4-ylamino)-1-oxopropan-2-yl)nicotinamide] 23

The polymerization of the diamine 9 with pyridine-3,5-dicarbonyl dichloride 15 produced the polymer 23 as a black solid, yield 67.0%, m. p. > 300°C, UV (DMSO): λmax= 268 nm (ε =957), λmax= 276 nm (ε =860), λmax= 322 nm (ε =179), IR (cm-1): 3416 (N-H, amide), 3087 (=C–H, aromatic), 2936 (C–H, aliphatic), 1669 (C=O, amide), 1593 and 1490 (C=C, aromatic), 1441 (C–N , aromatic), 1113 and 1070 (C–N, aliphatic). Calculated for C25H25N5O5; C, 63.15; H, 5.30; N, 14.73; Found: C, 63.33; H, 5.66; N, 14.99.

Poly[5-acetyl-N-((2S)-3-methyl-1-(4′-(3-methyl-2-(methylamino) butanamido)biphenyl-4-ylamino)-1-oxobutan-2-yl)nicotinamide] 24

The polymerization of the diamine 10 with pyridine-3,5-dicarbonyl dichloride 15 produced the polymer 24 as a black solid, yield 58.0%, m. p. > 300°C, UV (DMSO): λmax= 269 nm (ε =888), λmax= 276 nm (ε =731), IR (cm-1): 3420 (N-H, amide), 3036 (=C–H, aromatic), 2881 (C–H, aliphatic), 1639 (C=O, amide), 1612 and 1475 (C=C, aromatic), 1444 (C–N , aromatic), 1215 and 1150 (C–N , aliphatic). Calculated for C29H33N5O5; C, 65.52; H, 6.26; N, 13.17 Found: C, 65.17; H, 6.54; N, 13.51.

Poly[5-acetyl-N-((2S)-1-(4-(4-(2-(methylamino)propanamido)phenoxy) phenylamino)-1-oxopropan-2-yl)nicotinamide] 25

The polymerization of the diamine 11 with pyridine-3,5-dicarbonyl dichloride 15 produced the polymer 25 as a black solid, yield 54.0%, m. p. > 300°C, UV (DMSO): λmax= 269 nm (ε =1871), λmax= 367 nm (ε =166), IR (cm-1): 3440 (N-H, amide), 3085 (=C–H, aromatic), 2934 (C–H, aliphatic), 1668 (C=O, amide), 1591 and 1489 (C=C, aromatic), 1440 (C–N , aromatic), 1113 and 1070 (C–N , aliphatic). Calculated for C25H25N5O6; C, 61.09; H, 5.13; N, 14.25 Found: C, 60.98; H, 4.96; N, 14.63.

Results and discussion

Chemical preparation of the polyamides containing amino acids

Preparation of the Fmoc-protected diamines 5–8

The preparation of the new symmetric diamines 9–12, Scheme 1, for the stepwise polymerization was our first target. Fmoc-alanine (Fmoc-Ala-OH) 1 and Fmoc-valine (Fmoc-Val-OH) 2 were used in this investigation. Reactions of two equivalent amounts of the aforementioned amino acids with benzidine 3, or 4,4′-oxydianiline 4 were performed using two equivalents of HATU [37] as coupling reagent in presence of four equivalent of diisopropylethyl amine (DIEA) as base in dimethylformamide (DMF) to furnish the corresponding bis-Fmoc-protected diamines (5–8) in good yield and purity. The structures of the prepared protected diamines 5–8 were fully characterized by IR, 1H-NMR, 13C-NMR and elemental analyses. IR spectra of the protected diamines exhibited characteristic absorption bands in the range 3452–3288 cm−1 corresponding to the N-H bond. In addition the bands corresponding to the amide CONH group is observed in the range 1692–1668 cm−1. 1H-NMR spectra of compounds 5 8 in DMSO-d6 showed signals corresponding to four NH protons. The signals at the range δ 6.82-7.80 ppm correspond to two NH protons, and the other two NH protons are observed at the range δ 9.83-10.47 ppm. The 24 aromatic protons of compounds 5 and 6 are observed at the range δ 7.30-7.86 ppm, while those of compounds 7 and 8 are observed at the range 6.90-7.84 ppm. The 13C-NMR spectra of compounds 5 8 in DMSO-d6 show two signals corresponding to the four carbonyl groups at the range 152.99-154.00 ppm and at the range 174.29-175.60.

Scheme 1
scheme 1

Preparation of the diamines-containing amino acids 9–12.

Full size image

Preparation of the diamines-containing amino acids 9–12

Treatment of the protected diamines 5–8 with (3:7 Et2NH/CH3CN v/v) easily furnished the required diamines 9–12, respectively, in high yield, Scheme 1. Noteworthy, the byproduct dibenzofulvene was easily removed from the crude materials by washing with n-hexane. The crude products obtained were used as such without further purification.

Preparation of the polyamides 16–25 by low temperature solution polycondensation

The aromatic acid chlorides, namely isophthaloyl dichloride 13, pyridine-2,6-dicarbonyl dichloride 14, and pyridine-3,5-dicarbonyl dichloride 15 used in this investigation were prepared by the reaction of their corresponding dicarboxylic acids, isophthalic acid, pyridine-2,6-dicarboxylic acid, and pyridine-3,5-dicarboxylic acid respectively, with thionyl chloride in the presence of few drops of DMF. Direct polycondensation reaction of an equimolar mixture of the acid chloride 13 with the diamines 9–12 in DMAc solution at 0–5°C furnished the corresponding polyamides containing amino acids 16–19, respectively in high yields, Scheme 2. In a similar manner, reactions of the acid chlorides 14 and 15 with the diamines-containing amino acids 9–11 furnished the corresponding polyamides 20–22 and 23–25, Scheme 2. The polymer structures were confirmed by elemental analysis, IR and UV spectroscopy.

Scheme 2
scheme 2

Preparation of the polyamides 16–25 by low temperature solution polycondensation.

Full size image

Physical properties of the prepared polyamides containing amino acids

Solubility

The prepared polymers 16–25 showed similar solubility behavior in different organic solvents. Moderate to complete dissolution was observed in a variety of aprotic solvents such as NMP, DMSO, DMAc, boiling alcoholic solvents such as methanol, ethanol while insoluble in halogenated solvents such as CHCl3, CCl4, CH2Cl2, ClCH2CH2Cl or in ethers such as Et2O, THF, 1,4-dioxane or 1,2-dimethoxyethane (DME).

FTIR Spectroscopy

The FTIR spectra of the polymers exhibited characteristic absorbance at the range of υ 3477–3230 cm−1 and 1692–1639 cm−1, corresponding to the N-H and C = O stretching of the amide group, respectively. Bands around υ 2900 cm−1 were assigned to the alkyl H-C stretching, while bands appeared around υ 3050, 1598 and υ 1524 cm−1 assigned to the aromatic C-H and C=C aromatic, respectively.

Optical properties

The optical properties of polymers 16–25 were investigated by UV–vis spectroscopy in DMSO with a polymer concentration of 1 mg/10 mL. The spectra were recorded from 600 nm to 200 nm and the maximum absorbances (λmax) of the prepared polymers were recorded. Ala-containing polymers 18, 20, 23 and 25 exhibited bathochromic or red shifted peaks maxima at λ 362 nm, 321 nm, 322 nm and 367 nm, respectively may be attributed to the n→π transition while peaks at lower wavelengths appeared, respectively at 276 nm, 268 nm, 276 nm and 269 nm and could be attributed to the π→π transitions. 18 and 23 showed additional peak maxima at 268 nm, due to π→π transitions. Ala-containing polymers 16 and 22 exhibited peaks at wavelengths, appeared respectively at 304 nm and 276 nm which could be attributed to the π→π transitions. They also showed additional peak maxima at 272 nm and 268 nm due to π→π transitions.

Val-containing polymers 17, 19, 21 and 24 showed redshifted peaks maxima at λ 300 nm, 330 nm, 299 nm and 276 nm corresponding to the expected n→π, and similar peaks maxima at λ 275 nm, 268 nm, 275 nm and 269 nm, respectively due to π→π transitions.

Thermal properties

The thermal properties of these new materials were carried out in the temperature range from 20°C to 500°C in a stream of nitrogen atmosphere. Because many of the polymers containing amino acids were rather hydrophilic and could absorb atmospheric moisture during preparations, samples were heated to remove the absorbed water, cooled, and reheated again at a heating/cooling rate of 20°C/min.

Figures 1 and 2 show the TGA/DTG and DSC curves of the alanine-containing polymers 16, 20, 23 and valine-containing polymers 17, 21, 24, derived from the diamine 3, respectively. Structure-thermal property correlation based on changing the diacid residue revealed that the prepared polymers have comparable thermal stabilities. Alanine-containing polymers 16, 20, 23 exhibited subsequent degradation and their major amide linkage degradation processes appeared at 365°C (77.12% wt loss), 380°C (81.94% wt loss) and 375°C (86.74% wt loss) leaving 20.69%, 12.64% and 11.39%, respectively, as remaining mass residues. Valine-containing polymers 17, 21, 24 exhibited two subsequent major degradation processes appeared at [256°C (46.91% wt loss), 339°C (37.71% wt loss)] and [260°C (48.77% wt loss), 340°C (39.70% wt loss)] and [168°C (38.00% wt loss), 293°C (35.09% wt loss)] leaving 11.70%, 7.18% and 24.83%, respectively, as remaining mass residues. On the other hand, alanine-containing polymers 22 and 25 derived from the diamine 4 exhibited subsequent degradation processes appeared in the temperature ranges 219°C – 439°C (58.99% wt loss) and 300°C - 495°C (50.53% wt loss) leaving 19.69% and 37.57%, respectively, as remaining mass residues.

Figure 1
figure 1

TGA/DTG curves of the alanine-containing polymers 16, 20, 23 and valine-containing polymers 17, 21, 24.

Full size image
Figure 2
figure 2

DSC curves of the alanine-containing polymers 16, 20, 23 and valine-containing polymers 17, 21, 24.

Full size image

The glass transition temperature, T g , of the newly synthesized polymers ranged from 200°C to 225°C, and most of them were amorphous. In case of alanine-containing polymers 16, 20, 23, it is interesting to note that the change of the diacid had a noticeable Tg difference. In addition, pyridine-containing polymers 20 and 23 exhibited semicrystalline characteristic with melting temperature, T m , 383°C and 378°C, respectively. None of the valine-containing polymers 17, 21, 24 showed a melting and crystallization peak indicating that the polymers were amorphous. This is expected since L-valine side chain can inhibit close packing and eliminate crystallization.

Conclusions

The Thermal properties of the new types of polyamides based on benzene dicarboxylic acid, pyridine dicarboxylic acid, and α-amino acid (Alanine and Valine ) linked to benzidine and 4,4′-oxydianiline were evaluated by thermal gravimetric (TG), differential thermal gravimetric (DTG) and differential thermal analysis (DTA) techniques. Results revealed that structure-thermal property correlation based on changing the dicarboxylic acid monomer or the diamine monomer demonstrated an interesting connection between a single change (changing the dicarboxylic acids in each series while the diamine is fixed) and thermal properties. In addition, pyridine-containing polymers exhibited semicrystalline characteristic with melting temperature, T m . where none of the valine-containing polymers showed a melting and crystallization peak indicating that the polymers were amorphous. This is expected since L-valine side chain can inhibit close packing and eliminate crystallization. The newly prepared polymers may possess biodegradability and thus may find some applications as novel biomaterials.

References

  1. Chasin M, Langer R: Biodegradable polymers as drug delivery systems. 1990, NY: Marcel Dekker Inc

    Google Scholar 

  2. Huang SJ, Roby MS, Macri CA, Cameron JA: The effects of structure and morphology on the degradation of polymers with multiple groups. Biodegradable polymers and plastics. Edited by: Vert M, Feijen J, Albertsson A, Scott G, Chiellini E. 1992, Cambridge: The Royal Soc. of Chem, 149-157.

    Google Scholar 

  3. Bechaouch S, Coutin B, Sekiguchi H: Improvement of the synthesis of poly(L-cystyl-L-cystine): a new biodegradable polymer. Macromol Chem Phys. 1996, 197: 1661-1668. 10.1002/macp.1996.021970508.

    Article  CAS  Google Scholar 

  4. Bechaouch S, Gachard I, Coutin B, Sekiguchi H: Synthesis and degradation of nonpeptidic α-amino acid-containing polyamides. Polym Bull. 1997, 38: 365-370. 10.1007/s002890050061.

    Article  CAS  Google Scholar 

  5. Pascual S, Gachard I, Coutin B, Sekiguchi H: Synthesis of new polyamides from natural monomers: L-malic acid and L-Lysine. Macromol Chem Phys. 2001, 202: 873-881. 10.1002/1521-3935(20010301)202:6<873::AID-MACP873>3.0.CO;2-K.

    Article  CAS  Google Scholar 

  6. Mungara PM, Gonsalves KE: Synthesis of polyamides containing sites targeted for enzymatic cleavage. Polymer. 1994, 35: 663-666. 10.1016/0032-3861(94)90528-2.

    Article  CAS  Google Scholar 

  7. Nagata M, Kiyotsukuri T: Nylon-6 copolymers: copolymerization with α-amino acids. Eur Polym J. 1992, 28: 1069-1072. 10.1016/0014-3057(92)90058-A.

    Article  CAS  Google Scholar 

  8. Jin S, Mungara PM, Gonsalves KE: Synthesis of polyamides and polyureas containing leucine–tyrosine linkages. J Polym Sci Part A Polym Chem. 1997, 35: 499-507. 10.1002/(SICI)1099-0518(199702)35:3<499::AID-POLA13>3.0.CO;2-J.

    Article  CAS  Google Scholar 

  9. Langer R, Barrera DA, Zylstra E, Lansbury PT: Synthesis and RGD peptide modification of a new biodegradable copolymer –poly(lactic acid-co-lysine. J Am Chem Soc. 1993, 115: 11010-11011. 10.1021/ja00076a077.

    Article  Google Scholar 

  10. Noga DE, Petrie TA, Kumar A, Weck M, García AJ, Collard DM: Synthesis and modification of functional poly(lactide) copolymers: toward biofunctional materials. Biomacromolecules. 2008, 9: 2056-2062. 10.1021/bm800292z.

    Article  CAS  Google Scholar 

  11. Yoshida M, Asano M, Kumakura M, Katakai R, Mashimo T, Yuasa H, Yamaiaka H: Sequential polydepsipeptides containing tripeptide sequences and α-hydroxy acids as biodegradable carriers. Eur Polym J. 1991, 27: 325-329. 10.1016/0014-3057(91)90113-3.

    Article  CAS  Google Scholar 

  12. Bianco B, Castaldo L, Del Gaudio A, Maglio G, Palumbo R, La Cara F, Peluso G, Petillo O: Biocompatible α-amino acids based aliphatic polyamides. Polymer Bull. 1997, 39: 279-286. 10.1007/s002890050149.

    Article  CAS  Google Scholar 

  13. Castaldo L, Corbo P, Maglio G, Palumbo R: Synthesis and preliminary characterization of polyesteramides containing enzymatically degradable amide bonds. Polymer Bull. 1992, 28: 301-307. 10.1007/BF00294826.

    Article  CAS  Google Scholar 

  14. Maglio G, Maglio P, Oliva A, Palumbo R: Polyamides containing α-aminoacids and hydrophilic oxyethylene groups along the chain. Polymer Bull. 1999, 43: 191-198. 10.1007/s002890050552.

    Article  CAS  Google Scholar 

  15. Al-Khafaji JK, Ahmed MR, AL-Mousawy ZA: Preparation and characterization of new poly (( hexamethylene diamene – polyoxyethylene)) copolymers. Tikrit J Pure Sci. 2011, 16: 31-41.

    Google Scholar 

  16. Huang SJ, Bansleben DA, Knox JR: Biodegradable polymers: Chymotrypsin degradation of a low molecular weight poly(ester-urea) containing phenylalanine. J Appl Polym Sci. 1979, 23: 429-437. 10.1002/app.1979.070230212.

    Article  CAS  Google Scholar 

  17. Kartvelishvili T, Tsitlanadze G, Edilashvili L, Japaridze N, Katsarava R: Amino acid based bioanalogous polymers. Novel regular poly(ester urethane)s and poly(ester urea)s based on bis(L-phenylalanine) α, ω-alkylene diesters. Macromol Chem Phys. 1997, 198: 1921-1932. 10.1002/macp.1997.021980620.

    Article  CAS  Google Scholar 

  18. Sviridova LA, Leshcheva IF, Vertelov GK: Reaction of 1-acetyl-5-hydroxy-2-phenylpyrazolidines with amino acid esters. Chem Heterocycl Compd. 2000, 36: 1154-1160. 10.1023/A:1002808414124.

    Article  CAS  Google Scholar 

  19. Katsarava R, Beridze V, Arabuli N, Kharadze D, Chu CC, Won CY: Amino acid-based bioanalogous polymers. Synthesis, and study of regular poly(ester amide)s based on bis(α-amino acid) α, ω-alkylene diesters, and aliphatic dicarboxylic acids. J Polym Sci (A) Polym Chem. 1999, 37: 391-407. 10.1002/(SICI)1099-0518(19990215)37:4<391::AID-POLA3>3.0.CO;2-E.

    Article  CAS  Google Scholar 

  20. Ulbrich K, Strolham J, Kopecek J: Polymers containing enzymatically degradable bonds.10. poly(ethylene glycol)s containing enzymatically degradable bonds. Makromol Chem-Macromol Chem. Phys. 1986, 187: 1131-1144.

    Article  CAS  Google Scholar 

  21. Paredes N, Rodriguez-Galan A, Puigalli J: Synthesis and characterization of a family of biodegradable poly(ester amide)s derived from glycine. J Polym Sci Part A: Polym Chem. 1998, 36: 1271-1282. 10.1002/(SICI)1099-0518(199806)36:8<1271::AID-POLA10>3.0.CO;2-3.

    Article  CAS  Google Scholar 

  22. Paredes N, Casas MT, Puigalli J, Lotz B: Structural data on the packing of poly(ester amide)s derived from glycine, hexanediol, and odd-numbered dicarboxylic acids. J Polym Sci Part B: Polym Phys. 1999, 37: 2521-2533. 10.1002/(SICI)1099-0488(19990901)37:17<2521::AID-POLB23>3.0.CO;2-1.

    Article  CAS  Google Scholar 

  23. Asín L, Armelin E, Montané J, Rodríguez-Galán A, Puiggalí J: Sequential poly(ester amide)s based on glycine, diols, and dicarboxylic acids: thermal polyesterification versus interfacial polyamidation. Characterization of polymers containing stiff units. J Polym Sci Part A Polym Chem. 2001, 39: 4283-4293. 10.1002/pola.10082.

    Article  Google Scholar 

  24. Armelin E, Paracuellos N, Rodriguez-Galan A, Puiggali J: Study on the degradability of poly(ester amide)s derived from the α-amino acids glycine, and l-alanine containing a variable amide/ester ratio. Polymer. 2001, 42: 7923-7932. 10.1016/S0032-3861(01)00315-9.

    Article  CAS  Google Scholar 

  25. Botines E, Rodriguez-Galan A, Puiggali J: Poly(ester amide)s derived from 1,4-butanediol, adipic acid and 1,6-aminohexanoic acid: characterization and degradation studies. Polymer. 2002, 43: 6073-6084. 10.1016/S0032-3861(02)00577-3.

    Article  CAS  Google Scholar 

  26. Cianga L: Synthesis and characterization of optically active polymers containing azo groups and (l)-α-amino acid moieties. Eur Polym J. 2003, 39: 2271-2282. 10.1016/S0014-3057(03)00140-X.

    Article  CAS  Google Scholar 

  27. Karimi P, Rizkalla AS, Mequanint K: Versatile biodegradable poly(ester amide)s derived from α-amino acids for vascular tissue engineering. Materials. 2010, 3: 2346-2368. 10.3390/ma3042346.

    Article  CAS  Google Scholar 

  28. Puiggalí J, Subirana JA: Synthetic polymers containing α-amino acids: from polyamides to poly(ester amide). J Pep Sci. 2005, 11: 247-249. 10.1002/psc.642.

    Article  Google Scholar 

  29. Mallakpour S, Dinari M: Progress in synthetic polymers based on natural amino acids. J Macromol Sci Part A Pure and Applied Chemistry. 2011, 48: 644-679.

    Article  CAS  Google Scholar 

  30. Srinath D, Lin S, Knight DK, Rizkalla AS, Mequanint K: Fibrous biodegradable l-alanine-based scaffolds for vascular tissue engineering. Tissue Eng Regen Med. 2012, 10.1002/term.1562. Article first published online: 17 AUG 2012

    Google Scholar 

  31. Paredes N, Rodriguez-Galan A, Puigalli J, Peraire C: Studies on the biodegradation and biocompatibility of a new poly(ester amide) derived from L-alanine. J Appl Polym Sci. 1998, 69: 1537-1549. 10.1002/(SICI)1097-4628(19980822)69:8<1537::AID-APP8>3.0.CO;2-D.

    Article  CAS  Google Scholar 

  32. Rodriguez-Galan A, Pelfort M, Aceituno JE, Puigalli J: Comparative studies on the degradability of poly(ester amide)s derived from L- and L. D-alanine J Appl Polym Sci. 1999, 74: 2312-2320. 10.1002/(SICI)1097-4628(19991128)74:9<2312::AID-APP21>3.0.CO;2-0.

    Article  CAS  Google Scholar 

  33. Lips PAM, Broos R, van Heeringen MJM, Dijkstra PJ, Feijen J: Incorporation of different crystallizable amide blocks in segmented poly(ester amide)s. Polymer. 2005, 46: 7834-7842. 10.1016/j.polymer.2005.07.009.

    Article  CAS  Google Scholar 

  34. Puiggali J, Subirana JA: Synthetic polymers containing α-amino acids: from polyamides to poly(ester amides). J Pept Sci. 2005, 11: 247-249. 10.1002/psc.642.

    Article  CAS  Google Scholar 

  35. Mallakpour S, Zadehnazari A: Simple and efficient microwave-assisted polycondensation for preparation of chiral poly(amide-imide)s having pendant phenol moiety. Polym Sci (B ) Polym Chem. 2012, 54: 5-6.

    Google Scholar 

  36. Hassan HHAM, El-Husseiny AF, Abo-Elfadl AG, El-Faham A, Albericio F: Synthesis and thermal properties of Novel polyamides containing α-amino acid moieties: structure–property relationship. J Macromol Sci Part A. 2012, 49: 41-54.

    Article  CAS  Google Scholar 

  37. Carpino LA, El-Faham A: The diisopropylcarbodiimide/1-hydroxy- 7-azabenzotriazole system: segment coupling and stepwise peptide assembly. Tetrahedron. 1999, 1999 (55): 6813-6830.

    Article  Google Scholar 

Download references

Acknowledgment

This project was supported by King Saud University, Deanship of Scientific Research, College of Science Research Center.

Author information

Authors and Affiliations

  1. Department of Chemistry, College of Science, King Saud University, P.O. Box 2455, Riyadh, 11451, Kingdom of Saudi Arabia

    Ayman El-Faham

  2. Faculty of Science, Department of Chemistry, Alexandria University, P.O. Box 426, Ibrahimia, Alexandria, 21321, Egypt

    Ayman El-Faham, Hammed HAM Hassan & Sherine N Khattab

Authors
  1. Ayman El-Faham
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Hammed HAM Hassan
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Sherine N Khattab
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Ayman El-Faham.

Additional information

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

HAMH carried out the polymerization, SNK carried out the preparation of the monomers. AEF, HAMH and SNK designed the proposed methods and analyzed the data statistically together. All authors read and approved the final manuscript.

Electronic supplementary material

Additional file 1: FT-IR spectra of compound 5.(JPEG 308 KB)

Additional file 2: 1H NMR spectra of compound of compound 5.(TIFF 623 KB)

Additional file 3: 13C NMR spectra of compound of compound 5.(JPEG 318 KB)

Additional file 4: FT-IR spectra of compound 6.(TIFF 602 KB)

Additional file 5: 1H NMR spectra of compound of compound 6.(TIFF 704 KB)

Additional file 6: 13C NMR spectra of compound of compound 6.(TIFF 729 KB)

Additional file 7: FT-IR spectra of compound 7.(TIFF 723 KB)

Additional file 8: 1H NMR spectra of compound of compound 7.(TIFF 713 KB)

Additional file 9: 13C NMR spectra of compound of compound 7.(TIFF 710 KB)

Additional file 10: FT-IR of compound 8.(TIFF 751 KB)

Additional file 11: 1H NMR spectra of compound of compound 8.(TIFF 772 KB)

Additional file 12: 13C NMR spectra of compound of compound 8.(TIFF 786 KB)

Authors’ original submitted files for images

Below are the links to the authors’ original submitted files for images.

Authors’ original file for figure 1

Authors’ original file for figure 2

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Reprints and permissions

About this article

Cite this article

El-Faham, A., Hassan, H.H. & Khattab, S.N. Synthesis and characterization of new polyamides derived from alanine and valine derivatives. Chemistry Central Journal 6, 128 (2012). https://doi.org/10.1186/1752-153X-6-128

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/1752-153X-6-128

Keywords

BMC Chemistry

ISSN: 2661-801X

Contact us